Growth and superconducting properties of F-substituted ROBiS2 (R = La, Ce, Nd) single crystals

Masanori Nagao; Akira Miura; Satoshi Demura; Keita Deguchi; Satoshi Watauchi; Takahiro Takei; Yoshihiko Takano; Nobuhiro Kumada; Isao Tanaka

doi:10.1016/j.ssc.2013.10.019

Growth and superconducting properties of F-substituted ROBiS2 (R = La, Ce, Nd) single crystals

Masanori Nagao, Akira Miura, Satoshi Demura, Keita Deguchi, Satoshi Watauchi, Takahiro Takei, Yoshihiko Takano, Nobuhiro Kumada, Isao Tanaka

arXiv:1310.1213 · DOI 10.1016/j.ssc.2013.10.019 · 2013-10-04 · Solid State Communications

T1theoretical68 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

F-substituted ROBiS2 (R = La, Ce, Nd) superconducting single crystals with different F concentration were grown successfully using CsCl/KCl flux. All the obtained single crystals had a plate-like shape with a well-developed ab-plane of 1-2 mm in size. The flux components of Cs, K, and Cl were not detected in the obtained single crystals by electron probe microanalysis. The grown single crystals of F-substituted LaOBiS2 and CeOBiS2 showed superconducting at about 3 K while the Tc of the F-substituted NdOBiS2 exhibited approximately 5 K. The superconducting anisotropy of the single crystals of F-substituted LaOBiS2 and NdOBiS2 was estimated to be 30-45 according to the effective mass model whereas those values were 13-21 for the F-substituted CeOBiS2 single crystals. The F-substituted CeOBiS2 single crystals exhibited magnetic order at about 7 K that apparently coexisted with superconductivity below around 3 K.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
LaOBiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3	Pressure not reported	unknown
CeOBiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3	Pressure not reported	unknown
NdOBiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	5	Pressure not reported	unknown