Refinement of Nb3Sn grain size by the generation of ZrO2 precipitates in Nb3Sn wires
X. Xu, M. Sumption, X. Peng, E. W. Collings
arXiv:1402.3001 · DOI 10.1063/1.4866865 · 2014-02-12 · Applied Physics Letters
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
In this letter we demonstrate that if oxygen can be properly supplied to (Nb-Zr)-Sn wires, ZrO2 precipitates will form during the heat treatment, refining the Nb3Sn grain size markedly. Here, a Nb3Sn subelement was fabricated in which Nb-1Zr alloy was used, and oxygen was supplied via SnO2 powder. The results showed that such a design could supply sufficient oxygen to internally oxidize the Zr in the Nb-1Zr alloy, and that the sample reacted at 650 °C had grain sizes of ~45 nm, less than half the size of the grains in present Nb3Sn conductors. Magnetic measurements showed that the peak of the pinning force vs. field (Fp-B) curve was shifted to ~0.3Birr (the irreversibility field).
Similar papers
Performance Boost in Industrial Multifilamentary Nb3Sn Wires due to Radiation Induced Pinning Centers
similarity 0.86T. Baumgartner et al. · 2015 · arXiv:1504.05366
Source status unknown — claims are unverified
Beneficial influence of Hf and Zr additions to Nb4at.%Ta on the vortex pinning of NbSn with and without an O source
similarity 0.85Shreyas Balachandran et al. · 2018 · arXiv:1811.08867
Source status unknown — claims are unverified
A review and prospects for Nb3Sn superconductor development
similarity 0.83Xingchen Xu · 2017 · arXiv:1706.10253
Source status unknown — claims are unverified
Surface oxides, carbides, and impurities on RF superconducting Nb and Nb3Sn: A comprehensive analysis
similarity 0.82Zeming Sun et al. · 2023 · arXiv:2305.02467
Source status unknown — claims are unverified
Large decrease in the critical temperature of superconducting LaFeAsO0.85 compounds doped with 3% atomic weight of nonmagnetic Zn impurities
similarity 0.81Y. F. Guo et al.
Source status unknown — claims are unverified
Large decrease in the critical temperature of superconducting LaFeAsO0.85 compounds doped with 3% atomic weight of nonmagnetic Zn impurities
similarity 0.81Y. F. Guo et al. · 2010 · arXiv:1006.2874
Source status unknown — claims are unverified