A novel process to produce amorphous nano-sized B useful for MgB2 phase synthesis
Maurizio Vignolo, Gennaro Romano, Cristina Bernini, Alberto Martinelli, Antonio Sergio Siri
arXiv:1405.4112 · DOI 10.1109/TASC.2012.2190510 · 2014-05-16 · IEEE Transactions on Applied Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
In this paper we report a new synthesis route to produce boron powders characterized as being amorphous and having very fine particle size. This route has been developed to improve the performances of superconducting MgB2 powders, which can be directly synthesized from this nano-structured boron precursor by following the ex-situ or the in-situ P.I.T. method during the manufacturing of tapes, wires and cables. All the procedure steps are explained and the chemical-physical characterization of the boron powder, using x-ray diffraction (Xrd), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) techniques, is reported. Furthermore, a comparison with commercial boron is given. Preliminary results of the magnetic and electrical characterization, such as the critical temperature (TC) and the transport critical current density (JC t), for the MgB2 tape are reported and compared with the tape prepared with commercial boron.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
High temperature heat treatment of B precursor and P.I.T. process optimization to increase Jc performances of MgB2-based conductor
similarity 0.92Maurizio Vignolo et al. · 2014 · arXiv:1405.4099
Source status unknown — claims are unverified
In-situ high energy synchrotron X-ray diffraction investigation of the MgB2 phase formation and MgB2 tapes sintering
similarity 0.89Maurizio Vignolo et al. · 2014 · arXiv:1405.4134
Source status unknown — claims are unverified
Tube filling technique influence on superconductivity in MgB2-based conductors prepared using laboratory made boron
similarity 0.88Gianmarco Bovone et al. · 2014 · arXiv:1407.2111
Source status unknown — claims are unverified
Preparation and Superconductivity of a MgB2 Superconducting Tape
similarity 0.87G. C. Che et al. · 2001 · arXiv:cond-mat/0105215
Source status unknown — claims are unverified
High performance new MgB2 superconducting hollow wires
similarity 0.87G. Giunchi et al. · 2002 · arXiv:cond-mat/0207488
Source status unknown — claims are unverified
Thermal conductivity of MgB in the superconducting state
similarity 0.86M. Putti et al. · 2002 · arXiv:cond-mat/0210175
Source status unknown — claims are unverified