Tube filling technique influence on superconductivity in MgB2-based conductors prepared using laboratory made boron
Gianmarco Bovone, Davide Nardelli, Davide Matera, Maurizio Vignolo
arXiv:1407.2111 · 2014-06-12
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Here we report a systematic study of superconductive properties of mono-filamentary MgB2-based wires, manufactured with different filling technique. A detailed comparison of the influence of filling technique and final heat treatment on superconducting properties has been given. Boron used was synthesized in laboratory following magnesiothermic reduction of boron oxide, purified thanks to several acid leaching and heat treated at high temperature, to enhance crystalline degree. Critical current density and critical temperature have been investigated at different synthesis/sintering temperature in order to evaluate their dependence to applied final heat treatment. Critical current density has been evaluated on short wire pieces by magnetic measurement in a MPMS 5.5T Quantum Design SQUID, while critical temperature has been measured with a four probe system, by the drop of resistivity during the cooling of the sample in a liquid helium dewar.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
High performance new MgB2 superconducting hollow wires
similarity 0.90G. Giunchi et al. · 2002 · arXiv:cond-mat/0207488
Source status unknown — claims are unverified
Influence of the Preparation Process on Microstructure, Critical Current Density and Tc of MgB2 Powder-In-Tube Wires
similarity 0.90S. I. Schlachter et al. · 2002 · arXiv:cond-mat/0210591
Source status unknown — claims are unverified
Possibilities of MgB2/Cu Wires Fabricated by the in-situ Reaction Technique
similarity 0.89E. Martinez & R. Navarro · 2003 · arXiv:cond-mat/0306090
Source status unknown — claims are unverified
Influence of Preparation Process on Microstructure, Critical Current Density and Tc of MgB2/Fe/Cu Wires
similarity 0.89Y. F. Wu et al. · 2006 · arXiv:cond-mat/0607223
Source status unknown — claims are unverified
A novel process to produce amorphous nano-sized B useful for MgB2 phase synthesis
similarity 0.88Maurizio Vignolo et al. · 2014 · arXiv:1405.4112
Source status unknown — claims are unverified
Superconductivity in Dense MgB2 Wires
similarity 0.88P. C. Canfield et al.
Source status unknown — claims are unverified