Y. F. Wu, G. Yan, J. S. Li, Y. Feng, S. K. Chen, H. P. Tang, H. L. Xu, C. S. Li, P. X. Zhang, Y. F. Lu
arXiv:cond-mat/0607223 · DOI 10.4028/www.scientific.net/MSF.546-549.2031 · 2006-07-10 · Materials Science Forum
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The powder-in-tube MgB2 wires were prepared by high energy milling of Mg and B powder. The powder was not mechanically alloyed for 2h short milling time. However, the MgB2 grains in wires are very small (20 100nm) and resembled to the dimple after post-heat treatment. The clear evidence for transcrystlline fracture is observed. It indicated that the grain connection was greatly improved and the fluxing pinning was significantly enhanced. Another point to view is no intermediate annealing was adopted during the whole rolling process. The influence of the post-heat treatment on the transport current density was studied. Despite the lower Tc of about 35K, the transport current density reaches to 3X10E4A/cm2 at 15K and 3.5T for 700 sintered wires.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 35 | Pressure not reported | unknown |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 39 | Pressure not reported | unknown |
Similar papers
Superconducting properties of the powder-in-tube Cu-Mg-B and Ag-Mg-B wires
similarity 0.90B. A. Glowacki et al. · 2001 · arXiv:cond-mat/0109085
Source status unknown — claims are unverified
The Influence of Synthesis Parameters on Microstructures and Superconducting Properties of MgB2 Bulks
similarity 0.90Y. F. Wu et al. · 2006 · arXiv:cond-mat/0603536
Source status unknown — claims are unverified
Improved Superconducting Properties in Bulk MgB2 Prepared by High Energy Milling of Mg and B Powder
similarity 0.90Wu, Y. F. et al. · 2008 · arXiv:cond-mat/0607318
Source status unknown — claims are unverified
Superconductivity, critical current density, and flux pinning in MgB_{2-x}(SiC)_{x/2} superconductor after SiC nanoparticle doping
similarity 0.90S. X. Dou et al. · 2002 · arXiv:cond-mat/0207093
Source status unknown — claims are unverified
High-energy ball milling and synthesi temperature study to improve superconducting properties of MgB2 ex-situ tapes and wires
similarity 0.90Gennaro Romano et al. · 2008 · arXiv:0810.2438
Source status unknown — claims are unverified
Properties of superconducting MgB_2 wires: "in-situ" versus "ex-situ" reaction technique
similarity 0.90Alexey V Pan et al. · 2003 · arXiv:cond-mat/0302249
Source status unknown — claims are unverified