Improved Superconducting Properties in Bulk MgB2 Prepared by High Energy Milling of Mg and B Powder
Wu, Y. F., Lu, Y. F., Yan, G., Li, J. S., Feng, Y., Tang, H. P., Chen, S. K., Xu, H. L., Li, C. S., Zhang, P. X.
arXiv:cond-mat/0607318 · DOI 10.1088/0953-2048/19/11/021 · 2008-01-14 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The MgB2 bulks were prepared by high energy milling of Mg and B powder. The correlations among milling times, microstructure and superconducting properties were investigated in MgB2 bulks. Samples were characterized by x-ray diffraction (XRD), energy dispersive spectrometry (EDX) and scanning electron microscope (SEM), and the magnetization properties were examined by a Superconducting quantum interfere device (SQUID) magnetometer. It showed that the high energy milling is an effective approach to get fine crystalline (40-100nm) bulk MgB2 with good grain connectivity and high Jc performance. The critical current density reaches to 2.0X10E6A/cm2 at 15K and 0.59T, 5.7X10E5A/cm2 at 2T and 3.0X10E4A/cm2 at 5T.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
The Influence of Synthesis Parameters on Microstructures and Superconducting Properties of MgB2 Bulks
similarity 0.92Y. F. Wu et al. · 2006 · arXiv:cond-mat/0603536
Source status unknown — claims are unverified
Improved superconducting properties in nanocrystalline bulk MgB_2
similarity 0.91A. Gümbel et al. · 2001 · arXiv:cond-mat/0111585
Source status unknown — claims are unverified
Influence of Preparation Process on Microstructure, Critical Current Density and Tc of MgB2/Fe/Cu Wires
similarity 0.90Y. F. Wu et al. · 2006 · arXiv:cond-mat/0607223
Source status unknown — claims are unverified
Effect of grain refinement on enhancing critical current density and upper critical field in undoped MgB2 ex-situ tapes
similarity 0.90A. Malagoli et al. · 2008 · arXiv:0807.4078
Source status unknown — claims are unverified
Nanoscale grains, high irreversibility field, and large critical current density as a function of high energy ball milling time in C-doped magnesium diboride
similarity 0.90B. J. Senkowicz et al. · 2007 · arXiv:0712.2056
Source status unknown — claims are unverified
Improved superconducting properties of MgB2
similarity 0.90N. A. Frederick et al. · 2001 · arXiv:cond-mat/0106518
Source status unknown — claims are unverified