Effect of grain refinement on enhancing critical current density and upper critical field in undoped MgB2 ex-situ tapes
A. Malagoli, V. Braccini, M. Tropeano, M. Vignolo, C. Bernini, C. Fanciulli, G. Romano, M. Putti, C. Ferdeghini, E. Mossang, A. Polyanskii, D. C. Larbalestier
arXiv:0807.4078 · DOI 10.1063/1.3021468 · 2008-07-25 · Journal of Applied Physics
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Ex-situ Powder-In-Tube MgB2 tapes prepared with ball-milled, undoped powders showed a strong enhancement of the irreversibility field H*, the upper critical field Hc2 and the critical current density Jc(H) together with the suppression of the anisotropy of all of these quantities. Jc reached 104 A/cm2 at 4.2 K and 10 T, with an irreversibility field of about 14 T at 4.2 K, and Hc2 of 9 T at 25 K, high values for not-doped MgB2. The enhanced Jc and H* values are associated with significant grain refinement produced by milling of the MgB2 powder, which enhances grain boundary pinning, although at the same time also reducing the connectivity from about 12% to 8%. Although enhanced pinning and diminished connectivity are in opposition, the overall influence of ball milling on Jc is positive because the increased density of grains with a size comparable with the mean free path produces strong electron scattering that substantially increases Hc2, especially Hc2 perpendicular to the Mg and B planes.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Nanoscale grains, high irreversibility field, and large critical current density as a function of high energy ball milling time in C-doped magnesium diboride
similarity 0.92B. J. Senkowicz et al. · 2007 · arXiv:0712.2056
Source status unknown — claims are unverified
High-energy ball milling and synthesi temperature study to improve superconducting properties of MgB2 ex-situ tapes and wires
similarity 0.91Gennaro Romano et al. · 2008 · arXiv:0810.2438
Source status unknown — claims are unverified
Transport critical current, anisotropy, irreversibility fields and exponential n factors in Fe sheathed MgB2 tapes
similarity 0.91C. Beneduce et al. · 2002 · arXiv:cond-mat/0203551
Source status unknown — claims are unverified
Significantly enhanced critical current densities in MgB2 tapes made by a scaleable, nano-carbon addition route
similarity 0.91Yanwei Ma et al. · 2006 · arXiv:cond-mat/0601223
Source status unknown — claims are unverified
Improved Superconducting Properties in Bulk MgB2 Prepared by High Energy Milling of Mg and B Powder
similarity 0.90Wu, Y. F. et al. · 2008 · arXiv:cond-mat/0607318
Source status unknown — claims are unverified
Improved superconducting properties in nanocrystalline bulk MgB_2
similarity 0.90A. Gümbel et al. · 2001 · arXiv:cond-mat/0111585
Source status unknown — claims are unverified