Transport critical current, anisotropy, irreversibility fields and exponential n factors in Fe sheathed MgB2 tapes
C. Beneduce, H. L. Suo, P. Toulemonde, N. Musolino, R. Flukiger
arXiv:cond-mat/0203551 · 2002-03-27 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The influence of the initial MgB2 grain size on critical current density, upper critical fields and irreversibility has been studied on Fe sheathed monofilamentary MgB2 tapes prepared by the Powder-In-Tube technique. The effect of the reduction of MgB2 grain size by ball milling was mainly to enhance both the critical current density, jc, and the irreversibility field, while the upper critical field remained unchanged. The anisotropy ratio of the upper critical field between magnetic fields parallel and perpendicular the tape surface was determined to 1.3, reflecting a deformation induced texture. A good agreement has been found between resistive and inductive jc values, measured at various temperatures. At 25K and 1 T, jc values close to 105 A/cm2 were measured. The exponential n factor of the resistive transition was found to be quite high at low fields, and decrease linearly from 60 at 4T to 10 at 8.5T.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Transport Properties and Exponential n-values of Fe/MgB2 Tapes With Various MgB2 Particle Sizes
similarity 0.94P. Lezza et al. · 2003 · arXiv:cond-mat/0307398
Source status unknown — claims are unverified
Transport critical current densities and n factors in mono- and multifilamentary MgB2/Fe tapes and wires using fine powders
similarity 0.93H. L. Suo et al. · 2002 · arXiv:cond-mat/0208133
Source status unknown — claims are unverified
Effect of grain refinement on enhancing critical current density and upper critical field in undoped MgB2 ex-situ tapes
similarity 0.91A. Malagoli et al. · 2008 · arXiv:0807.4078
Source status unknown — claims are unverified
Fabrication and transport critical currents of multifilamentary MgB2/Fe wires and tapes
similarity 0.90H. L. Suo et al. · 2002 · arXiv:cond-mat/0203114
Source status unknown — claims are unverified
Critical Current Density and n-values of MgB2 Strands over a Wide Range of Temperatures and Fields
similarity 0.90G Z Li et al. · 2011 · arXiv:1108.5775
Source status unknown — claims are unverified
Electrical transport and anisotropic superconducting properties in single crystalline and dense polycrystalline MgB2
similarity 0.89A. K. Pradhan et al.
Source status unknown — claims are unverified