Fabrication and transport critical currents of multifilamentary MgB2/Fe wires and tapes
H. L. Suo, C. Beneduce, X. D. Su, R. Flukiger
arXiv:cond-mat/0203114 · DOI 10.1088/0953-2048/15/7/312 · 2002-03-06 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Multifilamentary MgB2/Fe wires and tapes with high transport critical current densities have been fabricated using a straightforward powder-in-tube (PIT) process. After annealing, we measured transport jc values up to 1.1 * 105 A/cm2 at 4.2 K and in a field of 2 T in a MgB2/Fe square wire with 7 filaments fabricated by two-axial rolling, and up to 5 * 104 A/cm2 at 4.2 K in 1 T in a MgB2/Fe tape with 7 filaments. For higher currents these multifilamentary wires and tapes quenched due to insufficient thermal stability of filaments. Both the processing routes and deformation methods were found to be important factors for fabricating multifilamentary MgB2 wires and tapes with high transport jc values.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Transport critical current densities and n factors in mono- and multifilamentary MgB2/Fe tapes and wires using fine powders
similarity 0.95H. L. Suo et al. · 2002 · arXiv:cond-mat/0208133
Source status unknown — claims are unverified
High transport critical current density obtained for Powder-In-Tube-processed MgB2 tapes and wires using stainless steel and Cu-Ni tubes
similarity 0.94H. Kumakura et al. · 2001 · arXiv:cond-mat/0106002
Source status unknown — claims are unverified
High transport currents in mechanically reinforced MgB2 wires
similarity 0.93W. Goldacker et al. · 2001 · arXiv:cond-mat/0106226
Source status unknown — claims are unverified
Preparation of 18-filament Cu/NbZr/MgB2 tape with high transport critical current density
similarity 0.91C. F. Liu et al. · 2001 · arXiv:cond-mat/0106061
Source status unknown — claims are unverified
Single-filament Composite MgB2/SUS Ribbons by Powder-In-Tube Process
similarity 0.90K. J. Song et al. · 2001 · arXiv:cond-mat/0106124
Source status unknown — claims are unverified
Fabrication of high performance MgB2 wires by an internal Mg diffusion process
similarity 0.90J. M. Hur et al. · 2007 · arXiv:0712.2273
Source status unknown — claims are unverified