High transport currents in mechanically reinforced MgB2 wires
W. Goldacker, S. I. Schlachter, S. Zimmer, H. Reiner
arXiv:cond-mat/0106226 · DOI 10.1088/0953-2048/14/9/331 · 2001-06-12 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self field. The reproducibility of the measured transport currents was excellent and not depending on the wire diameter. Using different precursors, commercial reacted powder or an unreacted Mg/B powder mixture, a strong influence on the pinning behaviour and the irreversibility field was observed. The critical transport current density showed a nearly linear temperature dependency for all wires being still 52 kA/cm^2 at 20 K and 23 kA/cm^2 at 30 K. Detailed data for Jc(B,T) and Tc(B) were measured.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure unresolved | unknown |
Similar papers
Mechanically reinforced MgB2 wires and tapes with high transport currents
similarity 0.93R. Nast et al. · 2001 · arXiv:cond-mat/0108458
Source status unknown — claims are unverified
Fabrication and transport critical currents of multifilamentary MgB2/Fe wires and tapes
similarity 0.93H. L. Suo et al. · 2002 · arXiv:cond-mat/0203114
Source status unknown — claims are unverified
Mechanical properties of reinforced MgB2 wires
similarity 0.91Wilfried Goldacker et al. · 2002 · arXiv:cond-mat/0211617
Source status unknown — claims are unverified
High transport critical current density obtained for Powder-In-Tube-processed MgB2 tapes and wires using stainless steel and Cu-Ni tubes
similarity 0.91H. Kumakura et al. · 2001 · arXiv:cond-mat/0106002
Source status unknown — claims are unverified
Transport and magnetic Jc of MgB2 strands and small helical coils
similarity 0.90M. D. Sumption et al. · 2004 · arXiv:cond-mat/0409651
Source status unknown — claims are unverified
Improvement of critical current in MgB2/Fe wires by a ferromagnetic sheath
similarity 0.90J. Horvat et al. · 2001 · arXiv:cond-mat/0109283
Source status unknown — claims are unverified