Transport and magnetic Jc of MgB2 strands and small helical coils
M. D. Sumption, M. Bhatia, M. Rindfleisch, M. Tomsic, E. W. Collings
arXiv:cond-mat/0409651 · DOI 10.1063/1.1875753 · 2004-09-24 · Applied Physics Letters
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The critical current densities of MgB2 monofilamentary strands with and without SiC additions were measured at 4.2 K. Additionally, magnetic Jc at B = 1 T was measured from 4.2 K to 40 K. Various heat treatment times and temperatures were investigated for both short samples and small helical coils. SiC additions were seen to improve high field transport Jc at 4.2 K, but improvements were not evident at 1 T at any temperature. Transport results were relatively insensitive to heat treatment times and temperatures for both short samples and coils in the 700C to 900C range.
Similar papers
Irreversibility Field and Flux Pinning in MgB2 with and Without SiC Additions
similarity 0.92M. D. Sumption et al. · 2004 · arXiv:cond-mat/0410301
Source status unknown — claims are unverified
Transport critical current density in Fe-sheathed nano-SiC doped MgB2 wires
similarity 0.92Shi X. Dou et al. · 2002 · arXiv:cond-mat/0208215
Source status unknown — claims are unverified
High transport currents in mechanically reinforced MgB2 wires
similarity 0.90W. Goldacker et al. · 2001 · arXiv:cond-mat/0106226
Source status unknown — claims are unverified
Transport Current in MgB2 based Superconducting Strand at 4.2 K and Self-Field
similarity 0.90M. D. Sumption et al. · 2001 · arXiv:cond-mat/0102441
Source status unknown — claims are unverified
Improved critical current densities in B4C doped MgB2 based wires
similarity 0.89P. Lezza et al. · 2006 · arXiv:cond-mat/0607073
Source status unknown — claims are unverified
Superconducting performance of ex-situ SiC-doped MgB2 mono-filamentary tapes
similarity 0.89Gennaro Romano et al. · 2014 · arXiv:1405.4124
Source status unknown — claims are unverified