Transport Current in MgB2 based Superconducting Strand at 4.2 K and Self-Field
M. D. Sumption, X. Peng, E. Lee, M. Tomsic, E. W. Collings
arXiv:cond-mat/0102441 · 2001-02-23 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Transport current values of 7.5 x 104 A/cm2 at 4.2 K and self-field are reported for MbB2-based tapes. MgB2 strands were formed by directly filling commercially available MgB2 powder into Nb-lined, monel tubes and wire drawing. The wires were then rolled into tapes 2.56 x 0.32 mm2, with a total superconducting cross section of 0.2319 mm2. Transport measurements were performed using a standard four-point technique at T = 4.2 K (in liquid helium) and at self field. Three samples were prepared, with heat treatments of 900C for 1, 2, and 3 h under 1/3 at Ar. Measured values of transport current were 4.7, 7.5, and 1.1 x 104 A/cm2, respectively, at 4.2 K and self field. M-H loops taken on the sample HT for 1 h showed magnetic Jcs of 4.2 x 104 A/cm2 at 4.2 K and 1 T, indicating that the material had reasonably well connected grains.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
High transport currents in mechanically reinforced MgB2 wires
similarity 0.90W. Goldacker et al. · 2001 · arXiv:cond-mat/0106226
Source status unknown — claims are unverified
Transport and magnetic Jc of MgB2 strands and small helical coils
similarity 0.90M. D. Sumption et al. · 2004 · arXiv:cond-mat/0409651
Source status unknown — claims are unverified
MgB2/Cu Racetrack Coil: Winding and Transport Testing
similarity 0.89M. D. Sumption et al. · 2004 · arXiv:cond-mat/0410450
Source status unknown — claims are unverified
Multifilamentary, in-situ Route, Cu-stabilized MgB2 Strands
similarity 0.89M. D. Sumption et al. · 2004 · arXiv:cond-mat/0409280
Source status unknown — claims are unverified
Fabrication and transport critical currents of multifilamentary MgB2/Fe wires and tapes
similarity 0.89H. L. Suo et al. · 2002 · arXiv:cond-mat/0203114
Source status unknown — claims are unverified
A New Approach for the Fabrication of MgB2 Superconducting Tape with Large In-field Transport Critical Current Density
similarity 0.89K. Komori et al. · 2002 · arXiv:cond-mat/0203113
Source status unknown — claims are unverified