MgB2/Cu Racetrack Coil: Winding and Transport Testing
M. D. Sumption, M. Bhatia, M. Rindfleisch, J. Phillips, M. Tomsic, E. W. Collings
arXiv:cond-mat/0410450 · 2004-10-18 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
A racetrack coil using MgB2/Cu strand has been fabricated and tested for transport current density at 4.2 K in self field. The monofilamentary strand was 1.0 mm OD and insulated with S-glass braid. Eighty turns of strand (42 m) were wound onto a stainless steel former with outer dimensions 25 cm x 10 cm x 0.86 cm. The resulting racetrack coil was heat treated at 675C for 30 minutes in flowing Ar. The strand, with a superconducting fraction of 26%, occupied 49% of the total coil pack cross sectional area. The coil Ic at 4.2 K and self field was 120 A (using a 1 microvolt/cm criterion). This led to a Jc,sc (across the whole coil) of 6.12 x 10^4 A/cm2, a Je in the wire of 1.59 x 10^4 A/cm2, and an overall winding Je of 7.9 x 10^3 A/cm2 at 4.2 K in self field. The n-values ranged from 17 to 56.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure unresolved | unknown |
Similar papers
Solenoidal Coils Made from Monofilamentary and Multifilamentary MgB2 strands
similarity 0.90M. D. Sumption et al. · 2005 · arXiv:cond-mat/0503755
Source status unknown — claims are unverified
Transport Current in MgB2 based Superconducting Strand at 4.2 K and Self-Field
similarity 0.89M. D. Sumption et al. · 2001 · arXiv:cond-mat/0102441
Source status unknown — claims are unverified
Transport and magnetic Jc of MgB2 strands and small helical coils
similarity 0.88M. D. Sumption et al. · 2004 · arXiv:cond-mat/0409651
Source status unknown — claims are unverified
High transport currents in mechanically reinforced MgB2 wires
similarity 0.87W. Goldacker et al. · 2001 · arXiv:cond-mat/0106226
Source status unknown — claims are unverified
Multifilamentary, in-situ Route, Cu-stabilized MgB2 Strands
similarity 0.86M. D. Sumption et al. · 2004 · arXiv:cond-mat/0409280
Source status unknown — claims are unverified
Large field generation with Hot Isostatically Pressed Powder-in-Tube MgB2 coil at 25 K
similarity 0.86A. Serquis et al. · 2004 · arXiv:cond-mat/0404052
Source status unknown — claims are unverified