Large field generation with Hot Isostatically Pressed Powder-in-Tube MgB2 coil at 25 K
A. Serquis, L. Civale, J. Y. Coulter, D. L. Hammon, X. Z. Liao, Y. T. Zhu, D. E. Peterson, F. M. Mueller, V. F. Nesterenko, S. S. Indrakanti
arXiv:cond-mat/0404052 · DOI 10.1088/0953-2048/17/10/L01 · 2004-04-02 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We present the fabrication and test results of Hot-Isostatic-Pressed (HIPed) Powder-in-Tube (PIT) MgB$_2$ coils. The coils properties were measured by transport and magnetization at different applied fields ($H$) and temperatures ($T$). The engineering critical current ($J_e$) value is the largest reported in PIT MgB$_2$ wires or tapes. At 25 K our champion 6-layer coil was able to generate a field of 1 T at self-field ($I_c >$ 220 A, $J_e \sim 2.8 \times 10^4$ A/cm$^2$). At 4 K this coil generated 1.6 T under an applied field of 1.25 T ($I_c \sim350$ A, $J_e \sim 4.5 \times 10^4$ A/cm$^2$). These magnetic fields are high enough for a superconducting transformer or magnet applications such as MRI. A SiC doped MgB$_2$ single layer coil shows a promising improvement at high fields and exhibits $J_c > 10^4$ A/cm$^2$ at 7 T.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
A Trapped Field of >3T in Bulk MgB2 Fabricated by Uniaxial Hot Pressing
similarity 0.89J. H. Durrell et al. · 2012 · arXiv:1207.6982
Source status unknown — claims are unverified
Fabrication and transport critical currents of multifilamentary MgB2/Fe wires and tapes
similarity 0.89H. L. Suo et al. · 2002 · arXiv:cond-mat/0203114
Source status unknown — claims are unverified
Hot isostatic pressing of powder in tube MgB2 wires
similarity 0.88A. Serquis et al. · 2003 · arXiv:cond-mat/0303043
Source status unknown — claims are unverified
Fabrication of small superconducting coils using (Ba,A)Fe2As2 (A: Na, K) round wires with large critical current densities
similarity 0.88Sunseng Pyon et al. · 2021 · arXiv:2106.10612
Source status unknown — claims are unverified
High transport critical current density above 30 K in pure Fe-clad MgB2 tape
similarity 0.88S. Soltanian et al. · 2001 · arXiv:cond-mat/0105152
Source status unknown — claims are unverified
Large transport critical currents in unsintered MgB2 superconducting tapes
similarity 0.87G. Grasso et al. · 2001 · arXiv:cond-mat/0103563
Source status unknown — claims are unverified