Hot isostatic pressing of powder in tube MgB2 wires
A. Serquis, L. Civale, D. L. Hammon, X. Z. Liao, J. Y. Coulter, Y. T. Zhu, M. Jaime, D. E. Peterson, F. M. Mueller, V. F. Nesterenko, Y. Gu
arXiv:cond-mat/0303043 · DOI 10.1063/1.1571231 · 2003-03-03 · Applied Physics Letters
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The critical current density (Jc) of hot isostatic pressed (HIPed) MgB2 wires, measured by d.c. transport and magnetization, is compared with that of similar wires annealed at ambient pressure. The HIPed wires have a higher Jc than the annealed wires, especially at high temperatures and magnetic fields, and higher irreversibility field (Hirr). The HIPed wires are promising for applications, with Jc>106 A/cm2 at 5 K and zero field and >104 A/cm2 at 1.5 T and 26.5 K, and Hirr ~ 17 T at 4 K. The improvement is attributed to a high density of structural defects, which are the likely source of vortex pinning. These defects, observed by transmission electron microscopy, include small angle twisting, tilting, and bending boundaries, resulting in the formation of sub-grains within MgB2 crystallites.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure unresolved | unknown |
Similar papers
Defect structures in MgB2 wires introduced by hot isostatic pressing
similarity 0.93X. Z. Liao et al. · 2003 · arXiv:cond-mat/0303009
Source status unknown — claims are unverified
Improved Hc2 in Bulk-Form Magnesium Diboride by Mechanical Alloying With Carbon
similarity 0.89B. J. Senkowicz et al. · 2004 · arXiv:cond-mat/0411199
Source status unknown — claims are unverified
Improved superconducting properties in nanocrystalline bulk MgB_2
similarity 0.89A. Gümbel et al. · 2001 · arXiv:cond-mat/0111585
Source status unknown — claims are unverified
Irreversibility Field and Flux Pinning in MgB2 with and Without SiC Additions
similarity 0.89M. D. Sumption et al. · 2004 · arXiv:cond-mat/0410301
Source status unknown — claims are unverified
Significant enhancement of irreversibility field in clean-limit bulk MgB2
similarity 0.89V. Braccini et al. · 2002 · arXiv:cond-mat/0208054
Source status unknown — claims are unverified
High transport currents in mechanically reinforced MgB2 wires
similarity 0.88W. Goldacker et al. · 2001 · arXiv:cond-mat/0106226
Source status unknown — claims are unverified