Improved Hc2 in Bulk-Form Magnesium Diboride by Mechanical Alloying With Carbon
B. J. Senkowicz, J. E. Giencke, S. Patnaik, C. B. Eom, E. E. Hellstrom, D. C. Larbalestier
arXiv:cond-mat/0411199 · DOI 10.1063/1.1920428 · 2004-11-08 · Applied Physics Letters
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
High energy milling of MgB2 pre-reacted powder renders the material largely amorphous through extreme mechanical deformation and is suitable for mechanically alloying MgB2 with dopants including carbon. Bulk samples of milled C and MgB2 powders subjected to hot isostatic pressing and Mg vapor annealing have achieved critical fields in excess of 32T and critical current density approaching 10^6 A/cm^2.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Nanoscale grains, high irreversibility field, and large critical current density as a function of high energy ball milling time in C-doped magnesium diboride
similarity 0.91B. J. Senkowicz et al. · 2007 · arXiv:0712.2056
Source status unknown — claims are unverified
Resistivity and Magneto-Optical Evidence for Variable and Incomplete Connectivity in Dense, High Critical Current Density C-alloyed Magnesium Diboride
similarity 0.90Senkowicz, B. J. et al. · 2006 · arXiv:cond-mat/0603800
Source status unknown — claims are unverified
Hot isostatic pressing of powder in tube MgB2 wires
similarity 0.89A. Serquis et al. · 2003 · arXiv:cond-mat/0303043
Source status unknown — claims are unverified
Improved superconducting properties in nanocrystalline bulk MgB_2
similarity 0.88A. Gümbel et al. · 2001 · arXiv:cond-mat/0111585
Source status unknown — claims are unverified
Comparative Study of Dense Bulk MgB Materials Prepared by Different Methods
similarity 0.88V. N. Narozhnyi et al. · 2002 · arXiv:cond-mat/0206513
Source status unknown — claims are unverified
High Critical Current Density and Improved Irreversibility Field in Bulk MgB2 Made By A Scaleable, Nanoparticle Addition Route
similarity 0.88J. Wang et al. · 2002 · arXiv:cond-mat/0204472
Source status unknown — claims are unverified