Resistivity and Magneto-Optical Evidence for Variable and Incomplete Connectivity in Dense, High Critical Current Density C-alloyed Magnesium Diboride
Senkowicz, B. J., Polyanskii, A. A., Mungall, R. J., Hellstrom, E. E., Larbalestier, D. C.
arXiv:cond-mat/0603800 · 2006-12-14
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Carbon-doped magnesium diboride was fabricated from pre-reacted pure MgB2 by mechanical alloying. The sample set had excellent critical current densities Jc(8T,4.2K) ranging from 15-60 kA/cm2, depending on composition. Magneto-optical imaging detected regions up to 0.5 mm in size which were nearly 100% dense with Jc 2-6 times that of the matrix. Evaluation of resistivity curves using the Rowell method predicts that only 10-50% of the cross sectional area carries the normal state measurement current, suggesting that considerable increases in Jc in these ~80% dense MgB2 samples would be possible with complete grain and particle connectivity.
Similar papers
Improved Hc2 in Bulk-Form Magnesium Diboride by Mechanical Alloying With Carbon
similarity 0.90B. J. Senkowicz et al. · 2004 · arXiv:cond-mat/0411199
Source status unknown — claims are unverified
Supercurrents in Magnesium Diboride/Metal Composite Wire
similarity 0.89M. J. Holcomb · 2005 · arXiv:cond-mat/0506779
Source status unknown — claims are unverified
Nanoscale grains, high irreversibility field, and large critical current density as a function of high energy ball milling time in C-doped magnesium diboride
similarity 0.87B. J. Senkowicz et al. · 2007 · arXiv:0712.2056
Source status unknown — claims are unverified
High transport currents in mechanically reinforced MgB2 wires
similarity 0.87W. Goldacker et al. · 2001 · arXiv:cond-mat/0106226
Source status unknown — claims are unverified
Improved critical current densities in B4C doped MgB2 based wires
similarity 0.87P. Lezza et al. · 2006 · arXiv:cond-mat/0607073
Source status unknown — claims are unverified
Effect of oxygen incorporation on normal and superconducting properties of MgB2 films
similarity 0.87R. K. Singh et al. · 2008 · arXiv:0809.2297
Source status unknown — claims are unverified