Improved critical current densities in B4C doped MgB2 based wires
P. Lezza, C. Senatore, R. Flukiger
arXiv:cond-mat/0607073 · DOI 10.1088/0953-2048/19/10/007 · 2006-07-04 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
An improvement of the transport critical current density, Jc, of MgB2 wires was obtained after addition of 10 wt.% B4C powders, after reaction at 800 C: Jc values of 1.10^4 A/cm2 at 4.2 K and 9T were obtained for wires of 1.11 mm diameter in a Fe matrix. The starting mixture of Mg and B was doped with sub-micrometric B4C, the ratio being Mg : B : B4C = 1: 2 : 0.08, corresponding to 10 wt.% B4C. For T > 800 C, a decrease of Jc was found, due to the reaction with the Fe sheath. In order to investigate the origin of the improvement of the transport properties for heat treatments up to 800 C, X-ray diffraction measurements were performed. A decrease of the lattice constant a from 0.30854 nm to 0.30797 nm was found, thus suggesting an effect of the substitution of Carbon on the properties of the wires. A comparison with the literature data shows that the addition of B4C powders leads to the second highest improvement of Jc reported so far after SiC, thus constituting an alternative for future applications.
Similar papers
Simultaneous Addition of B4C + SiC to MgB2 Wires and Consequences for Jc and Birr
similarity 0.93Rene Fluekiger et al. · 2006 · arXiv:cond-mat/0608650
Source status unknown — claims are unverified
Enhancement of Critical Current Density in low level Al-doped MgB2
similarity 0.90A. Berenov et al. · 2004 · arXiv:cond-mat/0405567
Source status unknown — claims are unverified
Development of Doped MgB2 Wires and Tapes for Practical Applications
similarity 0.89Zhaoshun Gao et al. · 2010 · arXiv:1001.1219
Source status unknown — claims are unverified
Enhancement of in-field Jc in MgB2/Fe wire using single and multi-walled nanotubes
similarity 0.89J. H. Kim et al. · 2006 · arXiv:cond-mat/0607540
Source status unknown — claims are unverified
Role of Carbon in Enhancing the Performance of MgB2 superconductor
similarity 0.88V. P. S. Awana et al. · 2007 · arXiv:0708.3883
Source status unknown — claims are unverified
CVD routes to MgB2 conductors
similarity 0.88D. K. Finnemore et al. · 2003 · arXiv:cond-mat/0302242
Source status unknown — claims are unverified