Enhancement of Critical Current Density in low level Al-doped MgB2
A. Berenov, A. Serquis, X. Z. Liao, Y. T. Zhu, D. E. Peterson, Y. Bugoslavsky, K. A. Yates, M. G. Blamire, L. F. Cohen, J. L. MacManus-Driscoll
arXiv:cond-mat/0405567 · DOI 10.1088/0953-2048/17/10/001 · 2004-05-24 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Two sets of MgB2 samples doped with up to 5 at. % of Al were prepared in different laboratories using different procedures. Decreases in the a and c lattice parameters were observed with Al doping confirming Al substitution onto the Mg site. The critical temperature (Tc) remained largely unchanged with Al doping. For 1 - 2.5 at.% doping, at 20K the in-field critical current densities (Jc's) were enhanced, particularly at lower fields. At 5K, in-field Jc was markedly improved, e.g. at 5T Jc was enhanced by a factor of 20 for a doping level of 1 at.% Al. The improved Jcs correlate with increased sample resistivity indicative of an increase in the upper critical field, Hc2, through alloying.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Influence of Al doping on the critical fields and gap values in magnesium diboride single crystals
similarity 0.90T. Klein et al.
Source status unknown — claims are unverified
The different development of the anisotropic upper critical field in MgB2 by aluminum and carbon doping
similarity 0.90M. Angst et al. · 2004 · arXiv:cond-mat/0410722
Source status unknown — claims are unverified
Improved critical current densities in B4C doped MgB2 based wires
similarity 0.90P. Lezza et al. · 2006 · arXiv:cond-mat/0607073
Source status unknown — claims are unverified
Influence of Al doping on the critical fields and gap values in magnesium diboride single crystals
similarity 0.89T. Klein et al. · 2006 · arXiv:cond-mat/0604316
Source status unknown — claims are unverified
Increases in the Irreversibility Field and the Upper Critical Field of Bulk MgB2 by ZrB2 Addition
similarity 0.88M. Bhatia et al. · 2005 · arXiv:cond-mat/0503758
Source status unknown — claims are unverified
MgB2 single crystals substituted with Li and with Li-C: Structural and superconducting properties
similarity 0.88J. Karpinski et al.
Source status unknown — claims are unverified