CVD routes to MgB2 conductors

D. K. Finnemore, W. E. Straszheim, S. L. Bud'ko, P. C. Canfield, N. E. Anderson, R. J. Suplinskas

arXiv:cond-mat/0302242 · DOI 10.1016/S0921-4534(02)02325-0 · 2003-02-12 · Physica C-superconductivity and Its Applications

T2theoretical14 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Processing methods are described for the development of magnesium diboride wire using the chemical vapor deposition (CVD) to produce long lengths of suitably doped starting boron fiber. It is found that titanium can be co-deposited with the boron to make long lengths of doped fiber that contain both TiB and TiB2. When this fiber is reacted in Mg vapor to transform boron into MgB2, the resulting conductor has a superconducting critical current density of about 5 times 10^6 A/cm^2 at 5K and self field. The critical current density at 25K and 1 Tesla is 10,000 A/cm^2. Using optical methods to define grain boundaries and energy dispersive X-rays to determine Ti and Mg concentration, these samples show a fine dispersion of $Ti$ through out the grains and no conspicuous precipitation of TiB2 on the MgB2 grain boundaries. This is to be contrasted with the precipitation of TiB2 on MgB2 grain boundaries observed for samples prepared by solid state reaction of Ti, Mg, and B powders. Introducing Ti impurities into the B during the CVD deposition of the B gives a distribution of TiB2 in the resulting MgB2 different from solid state reaction of powders.

Source-reported materials — not catalogue approval

FormulaReported Tc (K)Pressure (GPa)Type
MgB2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

39.2Pressure not reportedunknown
Mg0.9Al0.1B2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

33Pressure not reportedunknown
MgB2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

38.2Pressure not reportedunknown
MgB1.94C0.06

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

34.8Pressure not reportedunknown
MgB2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

39Pressure not reportedunknown
MgB1.5C0.5

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

26Pressure not reportedunknown
MgB2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

36Pressure not reportedunknown
MgB2

Archive — visibility unverified

Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.

37Pressure not reportedunknown

Similar papers