Superconductivity in MgB_2 doped with Ti and C
R. H. T. Wilke, S. L. Bud'ko, P. C. Canfield, M. J. Kramer, Y. Q. Wu, D. K. Finnemore, R. J. Suplinskas, J. V. Marzik, S. T. Hannahs
arXiv:cond-mat/0411531 · DOI 10.1016/j.physc.2004.11.022 · 2004-11-22 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Measurements of the superconducting upper critical field, H_{c2}, and critical current density, J_c, have been carried out for MgB_2 doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance the superconducting performance. Carbon replaces boron in the MgB_2 lattice and apparently shortens the electronic mean free path thereby raising H_c2. Titanium forms precipitates of either TiB or TiB_2 that enhance the flux pinning and raise J_c. Most of these precipitates are intra-granular in the MgB_2 phase. If approximately 0.5% Ti and approximately 2% C are co-deposited with B to form doped boron fibers and these fibers are in turn reacted in Mg vapor to form MgB_2, the resulting superconductor has H_{c2}(T=0) ~ 25 T and J_c ~ 10,000 A/cm**2 at 5 K and 2.2 T.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
On Heavy Carbon Doping of MgB
similarity 0.90Deepa Kasinathan et al. · 2004 · arXiv:cond-mat/0409563
Source status unknown — claims are unverified
Systematic Effects of Carbon Doping on the Superconducting Properties of Mg(B1−xCx)2
similarity 0.89R. H. T. Wilke et al.
Source status unknown — claims are unverified
Titanium additions to MgB2 conductors
similarity 0.89N. E. Anderson, et al. · 2003 · arXiv:cond-mat/0302245
Source status unknown — claims are unverified
Intra-granular Ti precipitates in MgB2
similarity 0.89M. J. Kramer et al. · 2003 · arXiv:cond-mat/0302443
Source status unknown — claims are unverified
Superconductivity in Dense Wires
similarity 0.89P. C. Canfield et al. · 2001 · arXiv:cond-mat/0102289
Source status unknown — claims are unverified
Synthesis and Processing of powders and wires
similarity 0.89C. E. Cunningham et al. · 2001 · arXiv:cond-mat/0103390
Source status unknown — claims are unverified