Intra-granular Ti precipitates in MgB2
M. J. Kramer, S. L. Bud'ko, P. C. Canfield, R. H. T. Wilke, D. K. Finnemore, R. J. Suplinskas
arXiv:cond-mat/0302443 · 2003-02-21 · arXiv: Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Superconducting magnesium diboride has been prepared with intra-granular TiB precipitates that have appropriate size and spacing for the pinning of superconducting vortices. The TiB particles have a size ranging from 1 nm to 20 nm and a spacing about 5 times as large. By co-depositing Ti and B on a commercial carbon coated silicon carbide substrate with chemical vapor deposition methods, it was possible to obtain a starting fiber with Ti well dispersed in the B. Reacting these fibers in a Mg vapor then transformed the fiber into a superconductor capable of carrying 10,000 A/cm^2 at 25K and 1 T. The Ti-B bonds are strong enough that there is relatively little migration of the Ti as the MgB2 grains form around the TiB precipitates. TiB2 precipitates, if they are present, can not be seen in the selected area diffraction pictures that show the TiB precipitates.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 36 | Pressure not reported | onset |
Similar papers
Superconductivity in MgB_2 doped with Ti and C
similarity 0.88R. H. T. Wilke et al. · 2004 · arXiv:cond-mat/0411531
Source status unknown — claims are unverified
Titanium additions to MgB2 conductors
similarity 0.87N. E. Anderson, et al. · 2003 · arXiv:cond-mat/0302245
Source status unknown — claims are unverified
CVD routes to MgB2 conductors
similarity 0.87D. K. Finnemore et al. · 2003 · arXiv:cond-mat/0302242
Source status unknown — claims are unverified
Mg(B,O)2 precipitation in MgB2
similarity 0.86X. Z. Liao et al. · 2002 · arXiv:cond-mat/0212571
Source status unknown — claims are unverified
Grain boundary characteristics of Fe-based superconductors
similarity 0.86Kazumasa Iida et al. · 2020 · arXiv:2003.09146
Source status unknown — claims are unverified
Synthesis and Processing of powders and wires
similarity 0.85C. E. Cunningham et al. · 2001 · arXiv:cond-mat/0103390
Source status unknown — claims are unverified