Supercurrents in Magnesium Diboride/Metal Composite Wire
M. J. Holcomb
arXiv:cond-mat/0506779 · 2005-06-29
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We have fabricated a series of ex situ copper sheathed powder-in-tube MgB2 wires with 20% by volume Ag, Pb, In, and Ga metal added to the MgB2 powder. We find the transport critical current of these wires increases significantly with the addition of specific metals to the core filament. In particular, the critical current density (Jc) of the MgB2/Ga(20%) wire is in excess of 5x10^4 A/cm^2 at 10K in self field, nearly 50 times that of the MgB2/Ag(20%) wire. The temperature dependent Jc of all wires is well described as an ensemble of clean S/N/S junctions in which the relevant parameters are the average thickness of the N layer, the critical temperature of the S layer, and a scaling term related to Jc at zero temperature. Eliminating the differences in the filament microstructure as the primary cause of the enhanced Jc, we suggest that Jc is determined by the magnitude of the proximity effect induced superconductivity in the normal metal layer, which is known to be proportional to the electron-electron interaction in N. We present one-dimensional material specific calculations that support this, and zero-field cooled DC magnetic susceptibility data that confirm an increased number of well-connected superconducting grains exist in the composite wires that contain metal additions with large electron-electron interactions and long electron mean free paths.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure unresolved | unknown |
Similar papers
Improvement of critical current density in the Cu/MgB2 and Ag/MgB2 superconducting wires using the fast formation method
similarity 0.90S. Soltanian et al. · 2002 · arXiv:cond-mat/0201261
Source status unknown — claims are unverified
Possibilities of MgB2/Cu Wires Fabricated by the in-situ Reaction Technique
similarity 0.89E. Martinez & R. Navarro · 2003 · arXiv:cond-mat/0306090
Source status unknown — claims are unverified
Fabrication and transport critical currents of multifilamentary MgB2/Fe wires and tapes
similarity 0.89H. L. Suo et al. · 2002 · arXiv:cond-mat/0203114
Source status unknown — claims are unverified
Resistivity and Magneto-Optical Evidence for Variable and Incomplete Connectivity in Dense, High Critical Current Density C-alloyed Magnesium Diboride
similarity 0.89Senkowicz, B. J. et al. · 2006 · arXiv:cond-mat/0603800
Source status unknown — claims are unverified
Influence of the Preparation Process on Microstructure, Critical Current Density and Tc of MgB2 Powder-In-Tube Wires
similarity 0.89S. I. Schlachter et al. · 2002 · arXiv:cond-mat/0210591
Source status unknown — claims are unverified
Superconductivity in Dense Wires
similarity 0.88P. C. Canfield et al. · 2001 · arXiv:cond-mat/0102289
Source status unknown — claims are unverified