Improvement of critical current density in the Cu/MgB2 and Ag/MgB2 superconducting wires using the fast formation method
S. Soltanian, X. L. Wang, J. Horvat, A. H. Li, H. K. Liu, S. X. Dou
arXiv:cond-mat/0201261 · DOI 10.1016/S0921-4534(02)01881-6 · 2002-01-15 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The powder in tube method has been used to fabricate Ag and Cu clad MgB2 wires using an in-situ reaction method. The effects of short time sintering on the critical current densities of Ag and Cu clad MgB2 wires were studied. All the samples were examined using XRD, SEM, and magnetization measurements. For Ag clad wire Jc is improved by more than two times after the short time sintering process. Jc values of 1.2x10^5 A/cm2 in zero field and above 10^4 A/cm2 in 2T at 20 K have been achieved for Ag clad MgB2 wire which is only sintered for 6 minutes at 800oC. However, a remarkable degree of reaction has been found between the superconducting cores and the sheath materials, leading to the formation of Cu2Mg and Ag3Mg for copper and silver clad wires, respectively. The results from Tc, Jc and Hirr convincingly show that the short sintering causes less reaction between the magnesium and the sheath materials and markedly improves the critical current density. Our result shows that Iron is still the best sheath material because of the lack of reaction between Fe and the superconducting MgB2 material.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
High transport critical current density obtained for Powder-In-Tube-processed MgB2 tapes and wires using stainless steel and Cu-Ni tubes
similarity 0.90H. Kumakura et al. · 2001 · arXiv:cond-mat/0106002
Source status unknown — claims are unverified
Supercurrents in Magnesium Diboride/Metal Composite Wire
similarity 0.90M. J. Holcomb · 2005 · arXiv:cond-mat/0506779
Source status unknown — claims are unverified
Properties of superconducting MgB_2 wires: "in-situ" versus "ex-situ" reaction technique
similarity 0.90Alexey V Pan et al. · 2003 · arXiv:cond-mat/0302249
Source status unknown — claims are unverified
Influence of Preparation Process on Microstructure, Critical Current Density and Tc of MgB2/Fe/Cu Wires
similarity 0.89Y. F. Wu et al. · 2006 · arXiv:cond-mat/0607223
Source status unknown — claims are unverified
Superconducting properties of the powder-in-tube Cu-Mg-B and Ag-Mg-B wires
similarity 0.89B. A. Glowacki et al. · 2001 · arXiv:cond-mat/0109085
Source status unknown — claims are unverified
Large transport critical currents in unsintered MgB2 superconducting tapes
similarity 0.88G. Grasso et al. · 2001 · arXiv:cond-mat/0103563
Source status unknown — claims are unverified