High transport critical current density obtained for Powder-In-Tube-processed MgB2 tapes and wires using stainless steel and Cu-Ni tubes
H. Kumakura, A. Matsumoto, H. Fujii, K. Togano
arXiv:cond-mat/0106002 · DOI 10.1063/1.1407856 · 2001-06-01 · Applied Physics Letters
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
MgB2 tapes and wires were fabricated by the Powder-In-Tube method. Stainless steel and Cu-Ni tubes were used as sheath materials, and no heat treatment was applied. The tapes made of stainless steel showed transport critical current density Jc of about 10,000A/cm2 at 4.2K and 5T. A high Jc of about 300,000A/cm2 was obtained by extrapolating the Jc-B curves to zero field. Multifilamentary(7-core) MgB2 wire was successfully fabricated using Cu-Ni tubes. For both tapes and wires the grain connectivity of MgB2 was as good as a high-pressure sintered bulk sample. However, the Jc of the Cu-Ni sheathed wire was lower than the stainless steel sheathed tape due to the lower packing density of MgB2.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Fabrication and transport critical currents of multifilamentary MgB2/Fe wires and tapes
similarity 0.94H. L. Suo et al. · 2002 · arXiv:cond-mat/0203114
Source status unknown — claims are unverified
Large transport critical currents in unsintered MgB2 superconducting tapes
similarity 0.92G. Grasso et al. · 2001 · arXiv:cond-mat/0103563
Source status unknown — claims are unverified
Preparation of 18-filament Cu/NbZr/MgB2 tape with high transport critical current density
similarity 0.92C. F. Liu et al. · 2001 · arXiv:cond-mat/0106061
Source status unknown — claims are unverified
Significantly enhanced critical current densities in MgB2 tapes made by a scaleable, nano-carbon addition route
similarity 0.91Yanwei Ma et al. · 2006 · arXiv:cond-mat/0601223
Source status unknown — claims are unverified
High transport critical current density above 30 K in pure Fe-clad MgB2 tape
similarity 0.91S. Soltanian et al. · 2001 · arXiv:cond-mat/0105152
Source status unknown — claims are unverified
Transport critical current densities and n factors in mono- and multifilamentary MgB2/Fe tapes and wires using fine powders
similarity 0.91H. L. Suo et al. · 2002 · arXiv:cond-mat/0208133
Source status unknown — claims are unverified