Transport critical current densities and n factors in mono- and multifilamentary MgB2/Fe tapes and wires using fine powders
H. L. Suo, P. Lezza, D. Uglietti, C. Beneduce, V. Abacherli, R. Flukiger
arXiv:cond-mat/0208133 · DOI 10.1109/TASC.2003.812219 · 2002-08-07 · IEEE Transactions on Applied Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Mono- and multifilamentary MgB2/Fe tapes and wires with high transport critical current densities have been prepared using the powder-in-tube (PIT) process. The fabrication details are described. The effect of powder grain sizes and recrystallization temperature on jc has been investigated. At 25K and 1 T, jc values close to 105 A/cm2 were measured, while jc of 106 A/cm2 were extrapolated for 4.2K/0T in our monofilamentary tape. MgB2/Fe tapes exhibit high exponential n factors for the resistive transition: n ~ 80 and 40 were found at 5 T and 7 T, respectively. The highest transport jc values obtained so far in MgB2/Fe wires with 7 filaments were 1.1 * 105 A/cm2 at 4.2 K and in a field of 2 T, which is still lower than for monofilamentary tapes. Improved deformation and recovering processing is expected to lead to higher jc values.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Fabrication and transport critical currents of multifilamentary MgB2/Fe wires and tapes
similarity 0.95H. L. Suo et al. · 2002 · arXiv:cond-mat/0203114
Source status unknown — claims are unverified
Transport Properties and Exponential n-values of Fe/MgB2 Tapes With Various MgB2 Particle Sizes
similarity 0.93P. Lezza et al. · 2003 · arXiv:cond-mat/0307398
Source status unknown — claims are unverified
Transport critical current, anisotropy, irreversibility fields and exponential n factors in Fe sheathed MgB2 tapes
similarity 0.93C. Beneduce et al. · 2002 · arXiv:cond-mat/0203551
Source status unknown — claims are unverified
High transport critical current density obtained for Powder-In-Tube-processed MgB2 tapes and wires using stainless steel and Cu-Ni tubes
similarity 0.91H. Kumakura et al. · 2001 · arXiv:cond-mat/0106002
Source status unknown — claims are unverified
Significantly enhanced critical current densities in MgB2 tapes made by a scaleable, nano-carbon addition route
similarity 0.90Yanwei Ma et al. · 2006 · arXiv:cond-mat/0601223
Source status unknown — claims are unverified
High transport currents in mechanically reinforced MgB2 wires
similarity 0.90W. Goldacker et al. · 2001 · arXiv:cond-mat/0106226
Source status unknown — claims are unverified