Transport Properties and Exponential n-values of Fe/MgB2 Tapes With Various MgB2 Particle Sizes
P. Lezza, V. Abacherli, N. Clayton, C. Senatore, D. Uglietti, H. L. Suo, R. Flukiger
arXiv:cond-mat/0307398 · DOI 10.1016/j.physc.2003.09.060 · 2003-07-16 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Fe/MgB2 tapes have been prepared starting with pre-reacted binary MgB2 powders. As shown by resistive and inductive measurements, the reduction of particle size to a few microns by ball milling has little influence on Bc2, while the superconducting properties of the individual MgB2 grains are essentially unchanged. Reducing the particle size causes an enhancement of Birr from 14 to 16 T, while Jc has considerably increased at high fields, its slope Jc(B) being reduced. At 4.2K, values of 5.3*10^4 and 1.2*10^3 A/cm^2 were measured at 3.5 and 10 T, respectively, suggesting a dominant role of the conditions at the grain interfaces. A systematic variation of these conditions at the interfaces is undertaken in order to determine the limit of transport properties for Fe/MgB2 tapes. The addition of 5% Mg to MgB2 powder was found to affect neither Jc nor Bc2. For the tapes with the highest Jc values, very high exponential n factors were measured: n = 148, 89 and 17 at 3.5, 5 and 10T, respectively and measurements of critical current versus applied strain have been performed. The mechanism leading to high transport critical current densities of filamentary Fe/MgB2 tapes based on MgB2 particles is discussed.
Similar papers
Transport critical current, anisotropy, irreversibility fields and exponential n factors in Fe sheathed MgB2 tapes
similarity 0.94C. Beneduce et al. · 2002 · arXiv:cond-mat/0203551
Source status unknown — claims are unverified
Transport critical current densities and n factors in mono- and multifilamentary MgB2/Fe tapes and wires using fine powders
similarity 0.93H. L. Suo et al. · 2002 · arXiv:cond-mat/0208133
Source status unknown — claims are unverified
Fabrication and transport critical currents of multifilamentary MgB2/Fe wires and tapes
similarity 0.90H. L. Suo et al. · 2002 · arXiv:cond-mat/0203114
Source status unknown — claims are unverified
Effect of grain refinement on enhancing critical current density and upper critical field in undoped MgB2 ex-situ tapes
similarity 0.89A. Malagoli et al. · 2008 · arXiv:0807.4078
Source status unknown — claims are unverified
Large irreversibility field in nanoscale C-doped MgB2/Fe tape conductors
similarity 0.89Yanwei Ma et al. · 2006 · arXiv:cond-mat/0608308
Source status unknown — claims are unverified
High transport currents in mechanically reinforced MgB2 wires
similarity 0.89W. Goldacker et al. · 2001 · arXiv:cond-mat/0106226
Source status unknown — claims are unverified