High transport critical current density above 30 K in pure Fe-clad MgB2 tape
S. Soltanian, X. L. Wang, I. Kusevic, E. Babic, A. H. Li, H. K. Liu, E. W. Collings, S. X. Dou
arXiv:cond-mat/0105152 · DOI 10.1016/S0921-4534(01)00780-8 · 2001-05-07 · Physica C-superconductivity and Its Applications
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Fe-clad MgB2 long tapes have been fabricated using a powder-in-tube technique. An Mg + 2B mixture was used as the central conductor core and reacted in-situ to form MgB2. The tapes were sintered in pure Ar at 800 ^(o) C for 1 h at ambient pressure. SEM shows a highly dense core with a large grain size of 100 micron. The Fe clad tape shows a sharp transition with transition width of 0.2 K and Tc0 at 37.5 K. We have achieved the highest transport critical current reported so far at 1.6 times 10^(4) A/cm^2 for both 29.5 K in 1 Tesla and 33 K in null field. R-T and critical current were also measured for fields perpendicular and parallel to the tape plane. The iron cladding shielded on the core from the applied external field, with the shielding being less effective for the field in the tape plane. Fe cladding may be advantageous for some applications as it could reduce the effects of both the self-field and external fields.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 37.5 | Pressure unresolved | zero_resistance |
Similar papers
Large transport critical currents in dense Fe- and Ni-clad MgB2 superconducting tapes
similarity 0.95HongLi Suo et al. · 2001 · arXiv:cond-mat/0106341
Source status unknown — claims are unverified
Large transport critical currents in unsintered MgB2 superconducting tapes
similarity 0.93G. Grasso et al. · 2001 · arXiv:cond-mat/0103563
Source status unknown — claims are unverified
Fabrication and transport critical currents of multifilamentary MgB2/Fe wires and tapes
similarity 0.92H. L. Suo et al. · 2002 · arXiv:cond-mat/0203114
Source status unknown — claims are unverified
A New Approach for the Fabrication of MgB2 Superconducting Tape with Large In-field Transport Critical Current Density
similarity 0.91K. Komori et al. · 2002 · arXiv:cond-mat/0203113
Source status unknown — claims are unverified
Preparation of 18-filament Cu/NbZr/MgB2 tape with high transport critical current density
similarity 0.91C. F. Liu et al. · 2001 · arXiv:cond-mat/0106061
Source status unknown — claims are unverified
High transport critical current density obtained for Powder-In-Tube-processed MgB2 tapes and wires using stainless steel and Cu-Ni tubes
similarity 0.91H. Kumakura et al. · 2001 · arXiv:cond-mat/0106002
Source status unknown — claims are unverified