Defect structures in MgB2 wires introduced by hot isostatic pressing
X. Z. Liao, A. Serquis, Y. T. Zhu, L. Civale, D. L. Hammon, D. E. Peterson, F. M. Mueller, V. F. Nesterenko, Y. Gu
arXiv:cond-mat/0303009 · DOI 10.1088/0953-2048/16/7/310 · 2003-03-01 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The microstructures of MgB2 wires prepared by the powder-in-tube technique and subsequent hot isostatic pressing were investigated using transmission electron microscopy. Large amount of crystalline defects including small angle twisting, tilting, and bending boundaries, in which high densities of dislocations reside, were found forming sub-grains within MgB2 grains. It is believed that these defects resulted from particle deformation during the hot isostatic pressing process and are effective flux pinning centers that contribute to the high critical current densities of the wires at high temperatures and at high fields.
Similar papers
Hot isostatic pressing of powder in tube MgB2 wires
similarity 0.93A. Serquis et al. · 2003 · arXiv:cond-mat/0303043
Source status unknown — claims are unverified
The influence of structural defects on intra-granular critical currents of bulk MgB2
similarity 0.90A. Serquis et al. · 2003 · arXiv:cond-mat/0305027
Source status unknown — claims are unverified
Influence of the Preparation Process on Microstructure, Critical Current Density and Tc of MgB2 Powder-In-Tube Wires
similarity 0.88S. I. Schlachter et al. · 2002 · arXiv:cond-mat/0210591
Source status unknown — claims are unverified
Fabrication and transport critical currents of multifilamentary MgB2/Fe wires and tapes
similarity 0.86H. L. Suo et al. · 2002 · arXiv:cond-mat/0203114
Source status unknown — claims are unverified
Influence of Preparation Process on Microstructure, Critical Current Density and Tc of MgB2/Fe/Cu Wires
similarity 0.86Y. F. Wu et al. · 2006 · arXiv:cond-mat/0607223
Source status unknown — claims are unverified
The high gas pressure HIP influence on structure and transport properties of superconductors of single and multicore composition
similarity 0.86T. Cetner et al. · 2014 · arXiv:1406.2141
Source status unknown — claims are unverified