A Trapped Field of >3T in Bulk MgB2 Fabricated by Uniaxial Hot Pressing
J. H. Durrell, C. E. J. Dancer, A. Dennis, Y. Shi, Z. Xu, A. M. Campbell, N. H. Babu, R. I. Todd, C. R. M. Grovenor, D. A. Cardwell
arXiv:1207.6982 · DOI 10.1088/0953-2048/25/11/112002 · 2012-07-30 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
A trapped field of over 3 T has been measured at 17.5 K in a magnetised stack of two disc-shaped bulk MgB2 superconductors of diameter 25 mm and thickness 5.4 mm. The bulk MgB2 samples were fabricated by uniaxial hot pressing, which is a readily scalable, industrial technique, to 91% of their maximum theoretical density. The macroscopic critical current density derived from the trapped field data using the Biot-Savart law is consistent with the measured local critical current density. From this we conclude that critical current density, and therefore trapped field performance, is limited by the flux pinning available in MgB2, rather than by lack of connectivity. This suggests strongly that both increasing sample size and enhancing pinning through doping will allow further increases in trapped field performance of bulk MgB2.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
MgB2 bulk superconducting magnet
similarity 0.92A. Yamamoto et al. · 2012 · arXiv:1208.1854
Source status unknown — claims are unverified
Temperature dependence of trapped magnetic field in MgB2 bulk superconductor
similarity 0.90R. V. Viznichenko et al. · 2003 · arXiv:cond-mat/0307318
Source status unknown — claims are unverified
Large field generation with Hot Isostatically Pressed Powder-in-Tube MgB2 coil at 25 K
similarity 0.89A. Serquis et al. · 2004 · arXiv:cond-mat/0404052
Source status unknown — claims are unverified
Comparative Study of Dense Bulk MgB Materials Prepared by Different Methods
similarity 0.89V. N. Narozhnyi et al. · 2002 · arXiv:cond-mat/0206513
Source status unknown — claims are unverified
Thin Film Magnesium Boride Superconductor with Very High Critical Current Density and Enhanced Irreversibility Field
similarity 0.88C. B. Eom et al. · 2001 · arXiv:cond-mat/0103425
Source status unknown — claims are unverified
Magnetic field processing to enhance critical current densities of MgB2 superconductors
similarity 0.88S. X. Dou et al. · 2006 · arXiv:cond-mat/0601191
Source status unknown — claims are unverified