High-energy ball milling and synthesi temperature study to improve superconducting properties of MgB2 ex-situ tapes and wires
Gennaro Romano, Maurizio Vignolo, Valeria Braccini, Cristina Bernini, Andrea Malagoli, Matteo Tropeano, Carlo Fanciulli, Marina Putti, Carlo Ferdeghini
arXiv:0810.2438 · DOI 10.1109/TASC.2009.2019133 · 2008-10-14
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
MgB2 monofilamentary nickel-sheated tapes and wires were fabricated by means of the ex-situ powder-in-tube method using either high-energy ball milled and low temperature synthesized powders. All sample were sintered at 920 C in Ar flow. The milling time and the revolution speed were tuned in order to maximize the critical current density in field (Jc): the maximum Jc value of 6 x 10e4 A/cm2 at 5 K and 4 T was obtained corresponding to the tape prepared with powders milled for 144h at 180rpm. Vorious synthesis temperature were also investigated (730-900 C) finding a best Jc value for the wire prepared with powders synthesized at 745 C. We speculate that this optimal temperature is due to the fluidifying effect of unreacted magnesium content before the sintering process which could better connect the grains.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Effect of grain refinement on enhancing critical current density and upper critical field in undoped MgB2 ex-situ tapes
similarity 0.91A. Malagoli et al. · 2008 · arXiv:0807.4078
Source status unknown — claims are unverified
Improved Superconducting Properties in Bulk MgB2 Prepared by High Energy Milling of Mg and B Powder
similarity 0.91Wu, Y. F. et al. · 2008 · arXiv:cond-mat/0607318
Source status unknown — claims are unverified
Influence of the Preparation Process on Microstructure, Critical Current Density and Tc of MgB2 Powder-In-Tube Wires
similarity 0.91S. I. Schlachter et al. · 2002 · arXiv:cond-mat/0210591
Source status unknown — claims are unverified
Influence of Preparation Process on Microstructure, Critical Current Density and Tc of MgB2/Fe/Cu Wires
similarity 0.91Y. F. Wu et al. · 2006 · arXiv:cond-mat/0607223
Source status unknown — claims are unverified
Enhanced critical current density of MgB2 superconductor synthesized in high magnetic fields
similarity 0.90Yanwei Ma et al. · 2006 · arXiv:cond-mat/0601245
Source status unknown — claims are unverified
Superconducting performance of ex-situ SiC-doped MgB2 mono-filamentary tapes
similarity 0.90Gennaro Romano et al. · 2014 · arXiv:1405.4124
Source status unknown — claims are unverified