First single crystal growth and structural analysis of superconducting layered bismuth oxyselenide; La(O,F)BiSe2

Masashi Tanaka; Masanori Nagao; Yoshitaka Matsushita; Masaya Fujioka; Saleem J. Denholme; Takahide Yamaguchi; Hiroyuki Takeya; Yoshihiko Takano

doi:10.1016/j.jssc.2014.07.026

First single crystal growth and structural analysis of superconducting layered bismuth oxyselenide; La(O,F)BiSe2

Masashi Tanaka, Masanori Nagao, Yoshitaka Matsushita, Masaya Fujioka, Saleem J. Denholme, Takahide Yamaguchi, Hiroyuki Takeya, Yoshihiko Takano

arXiv:1406.0734 · DOI 10.1016/j.jssc.2014.07.026 · 2014-06-03 · Journal of Solid State Chemistry

T1experimental26 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Single crystal of La(O,F)BiSe2 was successfully grown for the first time by the CsCl flux method. Single crystal X-ray structural analysis clearly showed that La(O,F)BiSe2 crystalizes with space group P4/nmm (lattice parameters a = 4.1408(2) Å, c = 14.1096(6) Å). The structure is composed of alternating BiSe2 and LaO layers. Magnetic susceptibility and resistivity measurements showed the superconducting transition at 3.6 K, which is higher than that of as-grown La(O,F)BiS2. The structural analysis implies that La(O,F)BiSe2 is potential superconductor having higher Tc under high pressure.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
La(O,F)BiSe2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3.6	Pressure not reported	unknown