Masanori Nagao

arXiv:1511.00219 · DOI 10.1515/nsm-2015-0007 · 2015-11-01 · Novel Superconducting Materials

T1theoretical22 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

R(O,F)BiS2 (R: La, Ce, Pr, Nd) superconducting single crystals with different F concentrations are grown using a CsCl/KCl flux. The obtained 1-2 mm-sized single crystals have a plate-like shape and are cleavable along the ab-plane. The crystal structure is tetragonal of space group P4/nmm (#129). The as-grown single crystals exhibit superconductivity at around 3-5 K. The superconducting transition temperature increases with decreasing the ionic radius of the R element. The superconducting anisotropies of the R(O,F)BiS2 single crystals are estimated to be 30-60 according to the effective mass model, whereas the anisotropies for Ce(O,F)BiS2 single crystals are 13-21. The c-axis transport measurements of a single crystal of Pr(O,F)BiS2 under a magnetic field parallel to the ab-plane reveal a "lock-in" state attributed to the Josephson vortex flow. Furthermore, the Ce(O,F)BiS2 single crystals exhibit a magnetic order at the temperature range of 5-7 K that apparently coexist with superconductivity below approximately 3 K.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
La(O,F)BiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4	Pressure not reported	unknown
Ce(O,F)BiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3	Pressure not reported	unknown
Pr(O,F)BiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4	Pressure not reported	unknown
Nd(O,F)BiS2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4	Pressure not reported	unknown