Effects of post-annealing and cobalt co-doping on superconducting properties of (Ca,Pr)Fe2As2 single crystals

Tomoyuki Okada; Hiraku Ogino; Hiroyuki Yakita; Akiyasu Yamamoto; Kohji Kishio; Jun-ichi Shimoyama

doi:10.1016/j.physc.2014.06.014

← Back to search

Effects of post-annealing and cobalt co-doping on superconducting properties of (Ca,Pr)Fe2As2 single crystals

Tomoyuki Okada, Hiraku Ogino, Hiroyuki Yakita, Akiyasu Yamamoto, Kohji Kishio, Jun-ichi Shimoyama

arXiv:1407.6441 · DOI 10.1016/j.physc.2014.06.014 · 2014-07-24 · Physica C-superconductivity and Its Applications

T1theoretical9 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

In order to clarify the origin of anomalous superconductivity in (Ca,RE)Fe2As2 system, Pr doped and Pr,Co co-doped CaFe2As2 single crystals were grown by the FeAs flux method. These samples showed two-step superconducting transition with Tc1 = 25~42 K, and Tc2 < 16 K, suggesting that (Ca,RE)Fe2As2 system has two superconducting components. Post-annealing performed for these crystals in evacuated quartz ampoules at various temperatures revealed that post-annealing at ~400°C increased the c-axis length for all samples. This indicates that as-grown crystals have a certain level of strain, which is released by post-annealing at ~400°C. Superconducting properties also changed dramatically by post-annealing. After annealing at 400°C, some of the co-doped samples showed large superconducting volume fraction corresponding to the perfect diamagnetism below Tc2 and high Jc values of 104~105 Acm-2 at 2 K in low field, indicating the bulk superconductivity of (Ca,RE)Fe2As2 phase occurred below Tc2. On the contrary, the superconducting volume fraction above Tc2 was always very small, suggesting that 40 K-class superconductivity observed in this system is originating in the local superconductivity in the crystal.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
(Ca,Pr)Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	33.5	Pressure not reported	unknown
(Ca,Pr)Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	16	Pressure not reported	unknown
(Ca,Pr,Co)Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	33.5	Pressure not reported	unknown
(Ca,Pr,Co)Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	16	Pressure not reported	unknown