Site Selectivity on Chalcogen Atoms in Superconducting La(O,F)BiSSe

Masashi Tanaka; Takuma Yamaki; Yoshitaka Matsushita; Masaya Fujioka; Saleem J. Denholme; Takahide Yamaguchi; Hiroyuki Takeya; Yoshihiko Takano

doi:10.1063/1.4915302

Site Selectivity on Chalcogen Atoms in Superconducting La(O,F)BiSSe

Masashi Tanaka, Takuma Yamaki, Yoshitaka Matsushita, Masaya Fujioka, Saleem J. Denholme, Takahide Yamaguchi, Hiroyuki Takeya, Yoshihiko Takano

arXiv:1412.8387 · DOI 10.1063/1.4915302 · 2014-12-29 · arXiv: Superconductivity

T1experimental29 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Single crystals of La(O,F)BiSSe were successfully grown by a CsCl flux method. Single crystal X-ray structural analysis revealed that the crystal structure is isostructural with BiS$_2$- or BiSe$_2$-based compounds with space group $P4/nmm$ (lattice parameters $a$ = 4.1110(2) Å, $c$ = 13.6010(7) Å). However, the S atoms are selectively occupied at the apical site of the Bi-SSe pyramids in the superconducting layer. The single crystals show a superconducting transition at 4.2 K in the magnetic susceptibility and resistivity measurement. The superconducting anisotropic parameter is determined to be 34 from its upper critical magnetic field. The anisotropy is in the same range with that of other members of the La(O,F)BiCh$_2$ ($Ch$ = S, Se) family under ambient pressure.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
La(O,F)BiSSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.2	Pressure unresolved	onset
La(O,F)BiSSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.2	Pressure unresolved	onset