Superconductivity in efficient thermoelectric Cu$_3$Sb$_{0.98}$Al$_{0.02}$Se$_4$

Xiao-Miao Zhao; Yong-Hui Zhou; Qiao-Wei Huang; Viktor V. Struzhkin; Ho-Kwang Mao; Alexander G. Gavriliuk; Xiao-Ying Qin; Di Li; Xi-Yu Li; Yuan-Yue Li; Xiao-Jia Chen

Superconductivity in efficient thermoelectric Cu$_3$Sb$_{0.98}$Al$_{0.02}$Se$_4$

Xiao-Miao Zhao, Yong-Hui Zhou, Qiao-Wei Huang, Viktor V. Struzhkin, Ho-Kwang Mao, Alexander G. Gavriliuk, Xiao-Ying Qin, Di Li, Xi-Yu Li, Yuan-Yue Li, Xiao-Jia Chen

arXiv:1501.03382 · 2015-01-13 · arXiv: Superconductivity

T2theoretical

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Both superconductivity and thermoelectricity offer promising prospects for daily energy efficiency applications. The advancements of thermoelectric materials have led to the huge improvement of the thermoelectric figure of merit in the past decade. By applying pressure on a highly efficient thermoelectric material Cu$_{3}$Sb$_{0.98}$Al$_{0.02}$Se$_4$, we achieve dome-shape superconductivity developing at around 8.5 GPa but having a maximum critical temperature of 3.2 K at pressure of 12.7 GPa. The novel superconductor is realized through the first-order structural transformation from its initial phase to an orthorhombic one. The superconducting phase is determined in the ultimate formation of the Cu-Al-Sb-Se alloy.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Cu3Sb0.98Al0.02Se4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	2.3	8.5 GPa	onset
Cu3Sb0.98Al0.02Se4 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	3.2	12.7 GPa	zero_resistance
MgB2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	40	Pressure not reported	unknown
PuCoGa5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	18.5	Pressure not reported	unknown
CsxRbyC60 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	33	Pressure not reported	unknown
Cs3C60 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38	Pressure not reported	unknown