Morphology of Superconducting FeSe thin films deposited by co-sputtering and MBE

Eike Venzmer; Alexander Kronenberg; Janek Maletz; Martin Jourdan

← Back to search

Morphology of Superconducting FeSe thin films deposited by co-sputtering and MBE

Eike Venzmer, Alexander Kronenberg, Janek Maletz, Martin Jourdan

arXiv:1505.02630 · 2015-05-11 · arXiv: Superconductivity

T2theoretical2 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The presumably unconventional superconductor Beta-FeSe was deposited by radio frequency sputtering and molecular beam epitaxy (MBE) from two elementary sources. Superconducting thin films were grown in (001)-orientation on MgO(100) and YAlO3(010) substrates. The morphology of the samples was studied and directly related to the superconducting properties of the Beta-FeSe thin films. The MBE grown thin films show microcracks down to the substrate and a roughness of about 100~nm. In contrast, sputter deposited superconducting thin films show a smooth surface with almost no precipitates. In both cases resistive superconducting transitions with critical temperature up to 8.5 K were observed. However, the smoothness of the sputter deposited films is crucial for future surface dependent investigations.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.5	Pressure not reported	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	11.8	Pressure not reported	onset
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8	Pressure not reported	midpoint
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	7.5	Pressure not reported	midpoint
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	5.8	Pressure not reported	midpoint
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8.5	Pressure not reported	unknown