Demonstration of an iron-pnictide bulk superconducting magnet capable of trapping over 1 T
J. D. Weiss, A. Yamamoto, A. A. Polyanskii, R. B. Richardson, D. C. Larbalestier, E. E. Hellstrom
arXiv:1510.02340 · DOI 10.1088/0953-2048/28/11/112001 · 2015-10-08 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
A trapped field of over 1 T at 5 K and 0.5 T at 20 K has been measured between a stack of magnetized cylinders of bulk polycrystalline Ba0.6K0.4Fe2As2 superconductors 10 mm in diameter and 18 mm in combined thickness. The trapped field showed a low magnetic creep rate (~3% after 24 hours at 5 K), while magneto-optical imaging revealed a trapped field distribution corresponding to uniform macroscopic current loops circulating through the sample. The superconductors were manufactured by hot isostatic pressing of pre-reacted powders using the scalable powder-in-tube technique. A high Vickers hardness of ~3.5 GPa and a reasonable fracture toughness of ~2.35 MPa m0.5 were measured. Given the untextured polycrystalline nature of the cylinders and their large irreversibility field (> 90 T), it is expected that larger bulks could trap fields in excess of 10 T.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Ba0.6K0.4Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
A Trapped Field of >3T in Bulk MgB2 Fabricated by Uniaxial Hot Pressing
similarity 0.89J. H. Durrell et al. · 2012 · arXiv:1207.6982
Source status unknown — claims are unverified
High-performance Ba1-xKxFe2As2 superconducting tapes with grain texture engineered via a scalable and cost-effective fabrication
similarity 0.88Shifa Liu et al. · 2021 · arXiv:2102.10829
Source status unknown — claims are unverified
Plastic pinning replaces collective pinning as the second magnetization peak disappears in the pnictide superconductor Ba0.75K0.25Fe2As2
similarity 0.86Shyam Sundar et al.
Source status unknown — claims are unverified
Magnetic Impurities in the Pnictide Superconductor BaKFeAs
similarity 0.86Sutirtha Mukhopadhyay et al. · 2009 · arXiv:0903.0674
Source status unknown — claims are unverified
High intrinsic flux pinning strength of BaFe2-xCoxAs2 superconductor
similarity 0.85K. Vinod et al. · 2011 · arXiv:1107.4170
Source status unknown — claims are unverified
High critical current density in textured Ba-122/Ag tapes fabricated by scalable rolling process
similarity 0.85Chiheng Dong et al. · 2014 · arXiv:1411.4720
Source status unknown — claims are unverified