Observation of high-Tc superconductivity in rectangular FeSe/STO(110) monolayer

P. Zhang; X. -L. Peng; T. Qian; P. Richard; X. Shi; J. -Z. Ma; B. -B. Fu; Y. -L. Guo; Z. Q. Han; S. C. Wang; L. L. Wang; Q. -K. Xue; J. P. Hu; Y. -J. Sun; H. Ding

doi:10.1103/PhysRevB.94.104510

Observation of high-Tc superconductivity in rectangular FeSe/STO(110) monolayer

P. Zhang, X. -L. Peng, T. Qian, P. Richard, X. Shi, J. -Z. Ma, B. -B. Fu, Y. -L. Guo, Z. Q. Han, S. C. Wang, L. L. Wang, Q. -K. Xue, J. P. Hu, Y. -J. Sun, H. Ding

arXiv:1512.01949 · DOI 10.1103/PhysRevB.94.104510 · 2015-12-07 · Physical Review B

T4theoretical31 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

It is well known that superconductivity in Fe-based materials is favoured under tetragonal symmetry, whereas competing orders such as spin-density-wave (SDW) and nematic orders emerge or are reinforced upon breaking the fourfold (C4) symmetry. Accordingly, suppression of orthorhombicity below the superconducting transition temperature (Tc) is found in underdoped compounds. Epitaxial film growth on selected substrates allows the design of crystal specific lattice distortions. Here we show that despite the breakdown of the C4 symmetry induced by a 5% difference in the lattice parameters, monolayers of FeSe grown by molecular beam epitaxy (MBE) on the (110) surface of SrTiO3 (STO) substrates [FeSe/STO(110)] exhibit a large nearly isotropic superconducting (SC) gap of 16 meV closing around 60 K. Our results on this new interfacial material, similar to those obtained previously on FeSe/STO(001), contradict the common belief that the C4 symmetry is essential for reaching high Tc's in Fe-based superconductors.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	60	Pressure not reported	onset
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	8	Pressure unresolved	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	37	Pressure not reported	unknown
FeSe Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	65	Pressure not reported	unknown