Mn-doping induced ferromagnetism and enhanced superconductivity in Bi_4-x Mn_x O_4 S_3 (0.075 < = x < = 0.15)

Zhenjie Feng; Xunqing Yin; Yiming Cao; Xianglian Peng; Tian Gao; Chuan Yu; Jingzhe Chen; Baojuan Kang; Bo Lu; Juan Guo; Qing Li; Wei-Shiuan Tseng; Zhongquan Ma; Chao Jing; Shixun Cao; Jincang Zhang; N. -C. Yeh

doi:10.1103/PhysRevB.94.064522

Mn-doping induced ferromagnetism and enhanced superconductivity in Bi_4-x Mn_x O_4 S_3 (0.075 < = x < = 0.15)

Zhenjie Feng, Xunqing Yin, Yiming Cao, Xianglian Peng, Tian Gao, Chuan Yu, Jingzhe Chen, Baojuan Kang, Bo Lu, Juan Guo, Qing Li, Wei-Shiuan Tseng, Zhongquan Ma, Chao Jing, Shixun Cao, Jincang Zhang, N. -C. Yeh

arXiv:1608.04410 · DOI 10.1103/PhysRevB.94.064522 · 2016-08-15 · Physical Review B

T1theoretical1 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

We demonstrate that Mn-doping in the layered sulfides Bi_4O_4S_3 leads to stable Bi_4-x Mn_x O_4 S_3 compounds that exhibit both long-range ferromagnetism and enhanced superconductivity for 0.075 < = x < = 0.15, with a possible record superconducting transition temperature (T_c) = 15 K among all BiS_2-based superconductors. We conjecture that the coexistence of superconductivity and ferromagnetism may be attributed to Mn-doping in the spacer Bi2O2 layers away from the superconducting BiS_2 layers, whereas the enhancement of T_c may be due to excess electron transfer to BiS_2 from the Mn4+/Mn3+-substitutions in Bi_2O_2. This notion is empirically corroborated by the increased electron-carrier densities upon Mn doping, and by further studies of the Bi_4-x A_x O_4 S_3 compounds (A = Co, Ni; x = 0.1, 0.125), where the T_c values remain comparable to that of the undoped Bi_4O_4S_3 system (= 4.5 K) due to lack of 4+ valences in either Co or Ni ions for excess electron transfer to the BiS_2 layers. These findings therefore shed new light on feasible pathways to enhance the T_c values of BiS_2-based superconductors.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Bi3.925Mn0.075O4S3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	15	Pressure unresolved	midpoint
Bi3.9Mn0.1O4S3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	15	Pressure unresolved	midpoint
Bi3.875Mn0.125O4S3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	15	Pressure unresolved	midpoint
Bi3.85Mn0.15O4S3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	15	Pressure unresolved	midpoint
Bi4O4S3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.5	Pressure unresolved	unknown
Bi3.875Co0.125O4S3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.8	Pressure unresolved	unknown
Bi3.875Co0.125O4S3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.8	Pressure unresolved	unknown
Bi3.875Ni0.125O4S3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.8	Pressure unresolved	unknown
Bi3.875Ni0.125O4S3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.8	Pressure unresolved	unknown