Impact of Fe site Co substitution on superconductivity of Fe1-xCoxSe0.5Te0.5 (x = 0.0 to 0.10): A flux free single crystal study
P. K. Maheshwari, Bhasker Gahtori, Anurag Gupta, V. P. S. Awana
arXiv:1610.08157 · DOI 10.1063/1.4972342 · 2016-10-26 · AIP Advances
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report synthesis of Co substitution at Fe site in Fe1-xCoxSe0.5Te0.5 (x=0.0 to 0.10) single crystals via vacuum shield solid state reaction route using flux free method. Single crystal XRD results showed that these crystals grow in (00l) plane i.e., orientation in c-direction. All the crystals possess tetragonal structure having P4/nmm space group. Detailed scanning electron microscopy (SEM) images show that the crystals are grown in slab-like morphology. The EDAX results revealed the final elemental composition to be near stoichiometric. Powder X-Ray diffraction (PXRD) Rietveld analysis results show that (00l) peaks are shifted towards higher angle with increasing Co concentration. Both a and c lattice parameters decrease with increasing Co concentration in Fe1-xCoxSe0.5Te0.5 (x=0.0 to 0.10) single crystals. Low temperature transport and magnetic measurements show that the superconducting transition temperature (Tc), decreases from around 12K to 10K and 4K for x=0.03 and x=0.05 respectively. For x=0.10 crystal superconductivity is not observed down to 2K.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| FeSe0.5Te0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 12 | Pressure not reported | unknown |
| FeSe0.5Te0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 12 | Pressure not reported | unknown |
| Fe0.97Co0.03Se0.5Te0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 10 | Pressure not reported | unknown |
| Fe0.97Co0.03Se0.5Te0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 10 | Pressure not reported | unknown |
| Fe0.95Co0.05Se0.5Te0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 4 | Pressure not reported | unknown |
| Fe0.95Co0.05Se0.5Te0.5 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 4 | Pressure not reported | unknown |
Similar papers
Effect of substitution and heat treatment route on polycrystalline FeSe0.5Te0.5 Superconductors
similarity 0.92Hacisalihoglu, Muammer Yasin & Yanmaz, Ekrem · 2012 · arXiv:1206.0401
Source status unknown — claims are unverified
Structural and Transport Studies of Under Doped FeTe1-xSex(x=0.0, 0.01, 0.03, 0.05) Single Crystals
similarity 0.90P. K. Maheshwari et al. · 2016 · arXiv:1601.04831
Source status unknown — claims are unverified
Superconducting and tetragonal-to-orthorhombic transitions in single crystals of FeSe1−xTex (0≤ x ≤0.61)
similarity 0.90Kotaro Terao et al.
Source status unknown — claims are unverified
Flux free growth of superconducting FeSe single crystals
similarity 0.90P. K. Maheshwari et al. · 2016 · arXiv:1606.08201
Source status unknown — claims are unverified
Effects of substituting Se with Te in the FeSe compound: structural, magnetization and Moessbauer studies
similarity 0.90R. W. Gómez et al. · 2009 · arXiv:0910.2504
Source status unknown — claims are unverified
Effect of Co Impurities on Superconductivity of FeSe0.4Te0.6 single crystals
similarity 0.89Fuyuki Nabeshima et al. · 2011 · arXiv:1107.0095
Source status unknown — claims are unverified