Probing Bulk Superconducting Order Parameter in Ba(K)Fe$_2$As$_2$ by Four Complementary Techniques

A. V. Muratov; T. E. Kuzmicheva; A. V. Sadakov; S. Yu. Gavrilkin; D. A. Knyazev; S. A. Kuzmichev; Yu. A. Aleshchenko; A. A. Kordyuk; V. M. Pudalov; M. Abdel-Hafiez

Probing Bulk Superconducting Order Parameter in Ba(K)Fe$_2$As$_2$ by Four Complementary Techniques

A. V. Muratov, T. E. Kuzmicheva, A. V. Sadakov, S. Yu. Gavrilkin, D. A. Knyazev, S. A. Kuzmichev, Yu. A. Aleshchenko, A. A. Kordyuk, V. M. Pudalov, M. Abdel-Hafiez

arXiv:1612.05540 · 2016-12-16 · arXiv: Superconductivity

T1experimental1 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

Using four different experimental techniques, we performed comprehensive studies of the bulk superconductive properties of single crystals of the nearly optimally doped $Ba_{1-x}K_xFe_2As_2$ ($T_{c} \approx 36\,K$), a typical representative of the 122 family. We investigated temperature dependencies of the (i) specific heat $C_{el}(T)$, (ii) first critical magnetic field $H_{c1}(T)$, (iii) intrinsic multiple Andreev reflection effect (IMARE), and (iv) infrared reflectivity spectra. All data clearly show the presence of (at least) two superconducting nodeless gaps. The quantitative data on the superconducting spectrum obtained by four different techniques are consistent with each other: (a) the small energy gap $Δ_S(0) \approx 1.8 - 2.5\,meV$, and the large gap energy $Δ_L(0) \approx 9.5 - 11.3\,meV$ that demonstrates the signature of an extended s-wave symmetry ($\sim~33 \%$ in-plane anisotropy), (b) the characteristic ratio $2Δ_L/k_BT_C$ noticeably exceeds the BCS value.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Ba0.67K0.33Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36.5	Pressure not reported	unknown
Ba0.67K0.33Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36.5	Pressure not reported	unknown
Ba0.67K0.33Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36.5	Pressure not reported	unknown
Ba0.65K0.35Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	36	Pressure not reported	unknown
Ba0.6K0.4Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	35.8	Pressure not reported	unknown
Ba0.68K0.32Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38.5	Pressure not reported	unknown
Ba0.65K0.35Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	34	Pressure not reported	unknown
Ba0.68K0.32Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38.5	Pressure not reported	unknown
Ba0.6K0.4Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	38	Pressure not reported	unknown
BaFe1.9Ni0.1As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	19	Pressure not reported	unknown
Ca0.32Na0.68Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	—