Superconducting joint between iron-based superconductor tapes
Yanchang Zhu, Dongliang Wang, Chundong Zhu, He Huang, Zhongtang Xu, Shifa Liu, Zhe Cheng, Yanwei Ma
arXiv:1805.03399 · 2018-05-09
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Superconducting joints are essential for iron-based superconductor's applications in future. In this study, a process for fabricating superconducting joints between Sr1-xKxFe2As2 (Sr-122) tapes is developed for the first time. The Ag sheath was peeled off from one side of each sample. The exposed superconducting parts of the two tapes were joined and wrapped again with Ag foil. The diffusion bonding of the iron-based superconducting joint was achieved by hot-pressing process in Argon atmosphere. The superconducting properties, microstructures and the elements distribution of the joint regions had been investigated. The pressure and pressing times were optimized in order to enhance the transport current of the joints. At 4.2 K and 10 T, a transport critical current Ic of 57 A for the joint was obtained, which is approximately 63.3% of the current capacity of the tapes themselves. Furthermore, the joint resistances dV/dI were estimated from the V-I curve of the joints and the calculated joint resistances values are below 10^-9 Ohm. These results demonstrate that the hot pressing was useful for fabricating the superconducting joint samples.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| Sr1-xKxFe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | — |
Similar papers
Large transport Jc in Cu-sheathed Sr0.6K0.4Fe2As2 superconducting tape conductors
similarity 0.89He Lin et al. · 2015 · arXiv:1504.02219
Source status unknown — claims are unverified
Large transport critical currents of powder-in-tube Sr0.6K0.4Fe2As2/Ag superconducting wires and tapes
similarity 0.88Lei Wang et al. · 2009 · arXiv:0911.3701
Source status unknown — claims are unverified
High transport Jc in magnetic fields up to 28 T of stainless steel/Ag double sheathed Ba122 tapes fabricated by scalable rolling process
similarity 0.87Zhaoshun Gao et al. · 2014 · arXiv:1412.1580
Source status unknown — claims are unverified
Achievement of practical level critical current densities in PIT Ba1-xKxFe2As2/Ag tapes by conventional cold mechanical deformation
similarity 0.87Zhaoshun Gao et al. · 2013 · arXiv:1310.4623
Source status unknown — claims are unverified
Improved transport critical currents in Ag and Pb co-doped BaxK1-xFe2As2 superconducting tapes
similarity 0.86Chao Yao et al. · 2012 · arXiv:1202.1039
Source status unknown — claims are unverified
Large Transport Critical Current Densities of Ag Sheathed (Ba,K)Fe2As2+Ag Superconducting Wires Fabricated by an ex-situ Powder-in-Tube (PIT) Process
similarity 0.84Kazumasa Togano et al. · 2011 · arXiv:1103.1701
Source status unknown — claims are unverified