Large Transport Critical Current Densities of Ag Sheathed (Ba,K)Fe2As2+Ag Superconducting Wires Fabricated by an ex-situ Powder-in-Tube (PIT) Process
Kazumasa Togano, Akiyoshi Matsumoto, Hiroaki Kumakura
arXiv:1103.1701 · DOI 10.1143/APEX.4.043101 · 2011-03-09 · Applied Physics Express
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report large transport critical current densities observed in Ag-added (Ba,K)Fe2As2 superconducting wires prepared by an ex-situ powder-in-tube (PIT) process. The wire has a simple composite structure sheathed only by Ag. A precursor bulk material prepared by a melting process was ground into powder and put into a Ag tube. The composite was then cold worked into a wire and heat treated at 850$^\circ$C for sintering. Transport critical current densities, Jc, at 4.2 K are 1.0\times104 A/cm2 (Ic = 60.7 A) in self field and 1.1\times103 A/cm2 (Ic = 6.6 A) in 10 T. These are the highest values reported so far for the Fe-based superconducting wires.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| (Ba,K)Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Large enhancement of transport critical current density of ex-situ PIT Ag/(Ba,K)Fe2As2 tapes achieved by applying cycles of cold deformation and heat treatment
similarity 0.93Kazumasa Togano et al. · 2013 · arXiv:1304.3161
Source status unknown — claims are unverified
Fabrication of small superconducting coils using (Ba,A)Fe2As2 (A: Na, K) round wires with large critical current densities
similarity 0.93Sunseng Pyon et al. · 2021 · arXiv:2106.10612
Source status unknown — claims are unverified
Superconducting properties and magneto-optical imaging of Ba0.6K0.4Fe2As2 PIT wires with Ag addition
similarity 0.93Qing-Ping Ding et al. · 2012 · arXiv:1201.5201
Source status unknown — claims are unverified
Enhanced high-field transport critical current densities observed for the ex-situ PIT processed Ag/(Ba,K)Fe2As2 thin tapes
similarity 0.93K. Togano et al. · 2013 · arXiv:1302.0482
Source status unknown — claims are unverified
Development of Powder-in-Tube Processed Iron Pnictide Wires and Tapes
similarity 0.93Yanwei Ma et al. · 2010 · arXiv:1008.1735
Source status unknown — claims are unverified
Large transport critical currents of powder-in-tube Sr0.6K0.4Fe2As2/Ag superconducting wires and tapes
similarity 0.93Lei Wang et al. · 2009 · arXiv:0911.3701
Source status unknown — claims are unverified