Development of Powder-in-Tube Processed Iron Pnictide Wires and Tapes
Yanwei Ma, Lei Wang, Yanpeng Qi, Zhaoshun Gao, Dongliang Wang, Xianping Zhang
arXiv:1008.1735 · DOI 10.1109/TASC.2010.2079311 · 2010-08-10 · IEEE Transactions on Applied Superconductivity
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
The development of the PIT fabrication process of iron pnictide superconducting wires and tapes has been carried out in order to enhance their transport properties. Silver was found to be the best sheath material, since no reaction layer was observed between the silver sheath and the superconducting core. The grain connectivity of iron pnictide wires and tapes has been markedly improved by employing Ag or Pb as dopants. At present, critical current densities in excess of 3750 A/cm^2 (Ic = 37.5 A) at 4.2 K have been achieved on Ag-sheathed SrKFeAs wires prepared with the above techniques, which is the highest in iron-based wires and tapes so far. Moreover, Ag-sheathed Sm-1111 superconducting tapes were successfully prepared by PIT method at temperatures as low as 900C, instead of commonly used temperatures of 1200C. These results demonstrate the feasibility of producing superconducting pnictide composite wires, even grain boundary properties require much more attention.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| SrKFeAs Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Large Transport Critical Current Densities of Ag Sheathed (Ba,K)Fe2As2+Ag Superconducting Wires Fabricated by an ex-situ Powder-in-Tube (PIT) Process
similarity 0.93Kazumasa Togano et al. · 2011 · arXiv:1103.1701
Source status unknown — claims are unverified
Large transport critical currents of powder-in-tube Sr0.6K0.4Fe2As2/Ag superconducting wires and tapes
similarity 0.92Lei Wang et al. · 2009 · arXiv:0911.3701
Source status unknown — claims are unverified
Fabrication and characterization of iron pnictide wires and bulk materials through the powder-in-tube method
similarity 0.92Yanwei Ma et al. · 2009 · arXiv:0906.3114
Source status unknown — claims are unverified
Strongly enhanced current densities in Sr0.6K0.4Fe2As2 superconducting tapes
similarity 0.92He Lin et al. · 2013 · arXiv:1309.7618
Source status unknown — claims are unverified
Development of high-performance iron-based superconducting wires and tapes
similarity 0.92Yanwei Ma · 2015 · arXiv:1506.00792
Source status unknown — claims are unverified
Large enhancement of transport critical current density of ex-situ PIT Ag/(Ba,K)Fe2As2 tapes achieved by applying cycles of cold deformation and heat treatment
similarity 0.91Kazumasa Togano et al. · 2013 · arXiv:1304.3161
Source status unknown — claims are unverified