Large enhancement of transport critical current density of ex-situ PIT Ag/(Ba,K)Fe2As2 tapes achieved by applying cycles of cold deformation and heat treatment
Kazumasa Togano, Zhaoshun Gao, Akiyoshi Matsumoto adn Hiroaki Kumakura
arXiv:1304.3161 · DOI 10.1088/0953-2048/26/11/115007 · 2013-04-10 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We report that high transport critical current density exceeding 104 A/cm2 at 4.2 K and 10 T can be obtained with good reproducibility for Ag sheathed (Ba,K)Fe2As2 (Ba 122) tapes by modifying the ex-situ powder-in-tube (PIT) method. The process involves cycles of the cold deformation and subsequent heat treatment. The intermediate cycles of flat rolling and heat treatment produce uniform fine-grained structure, resulting in an enhancement of transport Jc in applied magnetic fields. However, the rolled tapes contain cracks running traverse to the tape axis, which still limit the current pass along the tape axis. We found that the application of uniaxial pressing with small reduction rate at the final stage is very effective to heal those cracks, resulting in an extraordinary increase of the transport Jc. We achieved the highest Jc (at 4.2 K and 10 T) of 2.1x104 A/cm2 among the PIT processed Fe based wires and tapes reported so far. The Jc-H curves measured at higher temperatures maintains a small filed dependence up to around 20 K, suggesting that the tapes are promising for applications at higher temperatures as well as in liquid helium.
Similar papers
Enhanced high-field transport critical current densities observed for the ex-situ PIT processed Ag/(Ba,K)Fe2As2 thin tapes
similarity 0.97K. Togano et al. · 2013 · arXiv:1302.0482
Source status unknown — claims are unverified
Achievement of practical level critical current densities in PIT Ba1-xKxFe2As2/Ag tapes by conventional cold mechanical deformation
similarity 0.94Zhaoshun Gao et al. · 2013 · arXiv:1310.4623
Source status unknown — claims are unverified
Large Transport Critical Current Densities of Ag Sheathed (Ba,K)Fe2As2+Ag Superconducting Wires Fabricated by an ex-situ Powder-in-Tube (PIT) Process
similarity 0.93Kazumasa Togano et al. · 2011 · arXiv:1103.1701
Source status unknown — claims are unverified
Enhancement of Critical Current Densities in (Ba,K)Fe2As2 by 320 MeV Au Irradiation in Single Crystals and by High-Pressure Sintering in PIT Wires
similarity 0.91Sunseng Pyon et al. · 2013 · arXiv:1311.6213
Source status unknown — claims are unverified
Improved transport critical currents in Ag and Pb co-doped BaxK1-xFe2As2 superconducting tapes
similarity 0.91Chao Yao et al. · 2012 · arXiv:1202.1039
Source status unknown — claims are unverified
High critical current density and low anisotropy in textured Sr1-xKxFe2As2 tapes for high field applications
similarity 0.90Zhaoshun Gao et al. · 2013 · arXiv:1302.4583
Source status unknown — claims are unverified