Enhanced high-field transport critical current densities observed for the ex-situ PIT processed Ag/(Ba,K)Fe2As2 thin tapes
K. Togano, Z. S. Gao, H. Taira, S. Ishida, K. Kihou, A. Iyo, H. Eisaki, A. Matsumoto, H. Kumakura
arXiv:1302.0482 · DOI 10.1088/0953-2048/26/6/065003 · 2013-02-03 · Superconductor Science and Technology
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
We found that the transport Jc of the ex-situ PIT processed (Ba,K)Fe2As2 (Ba-122) wire with single Ag sheath can be significantly enhanced by repeating the combined process of rolling and heat treatment. The transport Jc (4.2 K and 10 T) of 4.4 x 103 A/cm2 (Ic =15.7 A) was obtained for a thin tape of 0.3 mm in thickness, which is the highest value reported so far for the PIT processed 122 wires and tapes with a Ag sheath and processed by a conventional route. The measurement by a hybrid magnet showed that Jc-H curve maintains very small field dependence up to the strong magnetic field of 28 T as expected from the previously reported high Hc2 value. The core of the thin tape shows dense grain structure with less cracks and voids and indicates the development of c-axis alignment, although it is still incomplete. The researches to elucidate the origin of Jc enhancement and to have further improvement of transport Jc are now ongoing. The process is simple using a Ag single sheath and, therefore, more realistic technique for long length wire production.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| (Ba,K)Fe2As2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | — | Pressure not reported | unknown |
Similar papers
Large enhancement of transport critical current density of ex-situ PIT Ag/(Ba,K)Fe2As2 tapes achieved by applying cycles of cold deformation and heat treatment
similarity 0.97Kazumasa Togano et al. · 2013 · arXiv:1304.3161
Source status unknown — claims are unverified
Achievement of practical level critical current densities in PIT Ba1-xKxFe2As2/Ag tapes by conventional cold mechanical deformation
similarity 0.93Zhaoshun Gao et al. · 2013 · arXiv:1310.4623
Source status unknown — claims are unverified
Large Transport Critical Current Densities of Ag Sheathed (Ba,K)Fe2As2+Ag Superconducting Wires Fabricated by an ex-situ Powder-in-Tube (PIT) Process
similarity 0.93Kazumasa Togano et al. · 2011 · arXiv:1103.1701
Source status unknown — claims are unverified
High transport current superconductivity in powder-in-tube Ba0.6K0.4Fe2As2 tapes at 27 tesla
similarity 0.91He Huang et al. · 2017 · arXiv:1705.09788
Source status unknown — claims are unverified
High transport Jc in magnetic fields up to 28 T of stainless steel/Ag double sheathed Ba122 tapes fabricated by scalable rolling process
similarity 0.91Zhaoshun Gao et al. · 2014 · arXiv:1412.1580
Source status unknown — claims are unverified
Fabrication of small superconducting coils using (Ba,A)Fe2As2 (A: Na, K) round wires with large critical current densities
similarity 0.91Sunseng Pyon et al. · 2021 · arXiv:2106.10612
Source status unknown — claims are unverified