Discovery of a new nontoxic cuprate superconducting system Ga-Ba-Ca-Cu-O
Yue Zhang, Wenhao Liu, Jin Si, Xiyu Zhu, Chengping He, Haonan Zhao, Hai-Hu Wen
arXiv:1805.09268 · DOI 10.1007/s11433-018-9249-1 · 2018-05-23 · Science China Physics, Mechanics & Astronomy
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Superconductivity is observed in a new nontoxic cuprate system Ga-Ba-Ca-Cu-O, with Tc = 82K for GaBa2Ca5Cu6O14+δ (Ga-1256) and Tc = 116K probably for GaBa2Ca3Cu4O10+δ (Ga-1234) or GaBa2Ca2Cu3O8+δ (Ga-1223), respectively. All compounds are fabricated by solid state reaction method under high pressure and high temperature. Samples are characterized by resistivity, magnetization and X-ray diffraction (XRD) measurements. The temperature dependence of magnetization measured in both zero-field-cooled and field-cooled processes on one sample (S1) shows two superconducting transitions at about 82K and 113K. The estimated shielding fraction for the phase with Tc of 82K is about 67%, while the fraction for another phase with Tc of 113K is quite small. The XRD Rietveld refinement for S1 indicates two main phases existing in the sample, Ga-1256 with fraction of about 58% and non-superconducting Ca0.85CuO2 with fraction of about 42%, respectively. Thus, we can conclude the superconducting phase with transition temperature of 82K is due to Ga-1256. The resistivity measurement also confirms the superconductivity for S1, and the resistivity reaches zero at about 82K. The temperature dependence of magnetization for another sample (S2) shows much higher superconducting shielding fraction for the phase with Tc of 116K, which may be a promising prospective for the synthesis of Ga-1234 or Ga-1223 phase.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| GaBa2Ca5Cu6O14+δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 82 | Pressure not reported | zero_resistance |
| GaBa2Ca5Cu6O14+δ Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 82 | Pressure not reported | onset |
Similar papers
Superconductivity above 130 K in the Hg-Pb-Ba-Ca-Cu-O system
similarity 0.87Z. Iqbal et al.
Source status unknown — claims are unverified
Preparation of the oxide superconductors (La,Gd,Ba,Ce)8Cu6Oz and (La,Gd,Ba,Sr,Ce)8Cu6Oz
similarity 0.87Takahiro Wada et al.
Source status unknown — claims are unverified
Calcium-substituted Y-Ba-Cu-O superconductors with enhanced Tc synthesized at elevated oxygen pressures
similarity 0.86D. E. Morris et al.
Source status unknown — claims are unverified
130-K superconductivity and microwave absorption in Tl-Ba-Ca-Cu-O
similarity 0.86Zhao Min-Guang & Yan Qi-Li
Source status unknown — claims are unverified
Characterization of the (Cu,C)BaCaCuO single crystals grown under high pressure
similarity 0.86Chengping He et al. · 2021 · arXiv:2111.11255
Source status unknown — claims are unverified
Superconductivity in the Mg-doped CuBa2Ca3Cu4O12−y system
similarity 0.85S. K. Agarwal et al.
Source status unknown — claims are unverified