Nodeless superconductivity in the noncentrosymmetric Mo$_3$Rh$_2$N superconductor: a $μ$SR study

T. Shang; Wesen Wei; C. Baines; J. L. Zhang; H. F. Du; M. Medarde; M. Shi; J. Mesot; T. Shiroka

doi:10.1103/PhysRevB.98.180504

← Back to search

Nodeless superconductivity in the noncentrosymmetric Mo$_3$Rh$_2$N superconductor: a $μ$SR study

T. Shang, Wesen Wei, C. Baines, J. L. Zhang, H. F. Du, M. Medarde, M. Shi, J. Mesot, T. Shiroka

arXiv:1811.01181 · DOI 10.1103/PhysRevB.98.180504 · 2018-11-03 · Physical Review B

T1theoretical11 citations

Active bibliographic source — not scientific approval

Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.

Abstract

The noncentrosymmetric superconductor Mo$_3$Rh$_2$N, with $T_c = 4.6$ K, adopts a $β$-Mn-type structure (space group $P$4$_1$32), similar to that of Mo$_3$Al$_2$C. Its bulk superconductivity was characterized by magnetization and heat-capacity measurements, while its microscopic electronic properties were investigated by means of muon-spin rotation and relaxation ($μ$SR). The low-temperature superfluid density, measured via transverse-field (TF)-$μ$SR, evidences a fully-gapped superconducting state with $Δ_0 = 1.73 k_\mathrm{B}T_c$, very close to 1.76 $k_\mathrm{B}T_c$ - the BCS gap value for the weak coupling case, and a magnetic penetration depth $λ_0 = 586$ nm. The absence of spontaneous magnetic fields below the onset of superconductivity, as determined by zero-field (ZF)-$μ$SR measurements, hints at a preserved time-reversal symmetry in the superconducting state. Both TF-and ZF-$μ$SR results evidence a spin-singlet pairing in Mo$_3$Rh$_2$N.

Source-reported materials — not catalogue approval

Formula	Reported Tc (K)	Pressure (GPa)	Type
Mo3Rh2N Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.6	Pressure not reported	onset
Mo3Rh2N Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.6	Pressure not reported	onset
Mo3Rh2N Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	4.6	Pressure not reported	onset
Li2Pd3B Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Li2Pt3B Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
CePt3Si Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
CeIrSi3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
K2Cr3As3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
LaNiC2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
(La,Y)2C3 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
(Ta,Nb)Rh2B2 Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown
Mo3Al2C Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula.	—	Pressure not reported	unknown