Enhancement of the superconducting critical temperature realized in the La-Ce-H system at moderate pressures
Wuhao Chen, Xiaoli Huang, Dmitrii V. Semenok, Su Chen, Kexin Zhang, Artem R. Oganov, Tian Cui
arXiv:2203.14353 · DOI 10.1038/s41467-023-38254-6 · 2022-03-27
Active bibliographic source — not scientific approval
Bibliographic access preserves source history; it does not approve extracted materials or validate reported claims. Review warnings on each occurrence separately.
Abstract
Covalent and ionic polyhydrides have become the two main camps in searching for the high-temperature superconductors under pressure. They have been considered as important platforms for exploring ternary or multiple hydrides in order to further increase the Tc or decrease the stabilization pressure. In this work, we successfully synthesized ternary hexagonal La-Ce polyhydrides stable in the pressure range of 95-130 GPa by laser-heating the La-Ce alloy (initial ratio La:Ce=2.5-3.5) in ammonia borane. Superconductivity at 176 K was strikingly preserved to about 100 GPa. The extrapolated upper critical field Hc2(0) reached 216 T at 100 GPa, the highest value among the synthesized polyhydrides. We also performed the contrast experiments and stabilized binary high-temperature superconducting LaHx with Tc-103 K at 78 GPa. In the pressure range of 95-130 GPa, the ternary hexagonal La-Ce-H system exhibits higher Tc than the binary La-H system, with the maximum difference of 100 K, and the compounds of both systems were synthesized at the same pressure and temperature conditions. These results clearly indicate that the discovered La-Ce-H system not only enriches the high-temperature superconducting hydrides but also realizes high-Tc at moderate pressures.
Source-reported materials — not catalogue approval
| Formula | Reported Tc (K) | Pressure (GPa) | Type |
|---|---|---|---|
| LaHx Archive — visibility unverified Source-occurrence policy only; no material identity or catalogue acceptance is inferred from the formula. | 103 | 78 GPa | unknown |
Similar papers
Potential high-Tc superconductors in the ternary Ce/Th-Sc-H system under pressure
similarity 0.92Guanlin Li et al.
Source status unknown — claims are unverified
Synthesis and superconductivity in (La,Ca)H10 under high pressure
similarity 0.91Su Chen et al.
Source status unknown — claims are unverified
High-temperature superconducting ternary Li−R−H superhydrides at high pressures (R=Sc,Y,La)
similarity 0.90Ying Sun et al.
Source status unknown — claims are unverified
Superconductivity at 215 K in lanthanum hydride at high pressures
similarity 0.90A. P. Drozdov et al. · 2018 · arXiv:1808.07039
Source status unknown — claims are unverified
Prediction of high-Tc superconductivity in ternary lanthanum borohydrides
similarity 0.90Xiaowei Liang et al.
Source status unknown — claims are unverified
Stability and Superconductivity of Ternary Polyhydrides
similarity 0.90Dmitrii V. Semenok et al. · 2025 · arXiv:2509.22877
Source status unknown — claims are unverified